In this study, organic and polymeric fluorophores based on 2,4,6-triphenylpyridiene (TPP) structure were found to have the novel aggregation-induced emission enhancement (AIEE) property. For the small-mass fluorophores, TPP and cyano-functionalized TPP (TPP-CN) were prepared from the facile Chichibabin reaction and their AIEE properties were characterized by the emission behavior in solvent/nonsolvent pair. Solid samples of TPP and TPP-CN exhibit enhanced emission with increasing annealing time under solvent vapors, thus, both compounds have the characters of crystallization-induced emission enhancement (CIEE) behavior. For polymeric system, copolymers PTPPF containing alternative TPP and 9,9-dioctylfluorene units were prepared through Suzuki coupling and study on its fluorescence behavior also reveals its AIEE feature. The rigid polymer possesses high emission intensity in its dilute solution state and remains almost unchanged with increasing nonsolvent fraction. The solid sample was found to have a high quantum yield (ФF) of 70 %.
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0713112-173820 |
Date | 13 July 2012 |
Creators | Li, Yi-wei |
Contributors | Ming Chen, Shiao-wei Kuo, Lieh-Li Lin, Jin-long Hong |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0713112-173820 |
Rights | user_define, Copyright information available at source archive |
Page generated in 0.0097 seconds