Currently, the International Technology Roadmap for Semiconductors (ITRS) is targeting the 22nm technology node in accordance with Moore’s Law. The low mobility of silicon makes it inherently unsuitable as a channel material for devices at this scale, and therefore a significant amount of research is being focused at re-evaluating germanium as an alternative substrate. Germanium offers a higher mobility than that of silicon and is compatible with existing silicon device manufacturing techniques. P-type ultra shallow junction (USJ) implemented in germanium exhibit low leakage currents and low sheet resistivity, satisfying the ITRS demands. However, N-type USJ formed using phosphorus as the dopant species do not yet satisfy these requirements due to a high diffusivity and low levels of electrical activation. This is due to the fact that at high phosphorus concentrations, the difference between the equilibrium solid solubility limit and the effective solid solubility is related to the formation of phosphorus-vacancy complexes. These evolve into electrically inactive clusters, by capturing the additional phosphorus resulting in an overall reduction of the electrical activity of the phosphorus population. Another problem is phosphorus out-diffusion during annealing process. In order to overcome these problems, novel techniques are currently being research. This thesis investigates the phosphorus activation and diffusion characteristics as a function of implant temperature and co-implantation of low dose germanium. The samples were subsequently subjected to an isochronal annealing before Hall Effect and SIMS analyses were performed to characterize the electrical activation and diffusion respectively. The results from the studies indicate that it is a non trivial process for germanium to replace silicon in order to become the next dominant substrate.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:644902 |
| Date | January 2015 |
| Creators | Razali, M. A. |
| Contributors | Gwilliam, R. |
| Publisher | University of Surrey |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://epubs.surrey.ac.uk/807317/ |
Page generated in 0.0024 seconds