Silicon carbide fibre/silicon nitride matrix composites have been fabricated using the reaction bonded silicon nitride (RBSN) and sintered reaction bonded silicon nitride (SRBSN) processing routes. A filament winding and tape casting system was developed to produce sheets of parallel aligned fibres within a layer of green matrix ('prepreg') which were cut, stacked and hot pressed to form a plate. This was nitrided and (in the case of SRBSN matrix composites) hot pressed at 1700°C to density the matrix. The magnesia (MgO) and the yttria/alumina (Y2O3/AI2O3) additive SRBSN systems were investigated as matrices for ease of processing and compatibility with the matrix. The MgO additive Si3N4 matrix reacted with the outer carbon rich layer on the surface of the fibres, framing a reaction layer approx. 2pm in thickness. A reaction layer was also observed with the Y2O3/AI2O3 additive matrix, but was thinner (< 0.5um), and was identified as silicon carbide from the electron diffraction pattern. X-ray mapping in the SEM was used to investigate the spatial distribution of elements within the interface region to a resolution < lum, including light elements such as carbon. The 6wt%Y203/ 2wt%Al203 additive SRBSN system was chosen for more detailed investigation, and the majority of characterisation was performed using this composition. Oxidation of composite samples was carried out at temperatures between 1000°C and 1400°C for up to 1000 hours. Little damage was visible after 100 hours for all temperatures, corresponding to a relatively small drop in post oxidation bend strength. After 1000 hours at 1000°C both carbon rich outer layers and the central carbon core of the fibre were removed. Samples were severely oxidised after 1000 hours at 1400°C, having a glass layer on the outer surface and replacement of near surface fibre/matrix interfaces with glass. The post oxidation bend strengths for both conditions were approx.2/3 of the as fabricated strength. Less damage was observed after 1000 hours at 1200°C, and the post oxidation bend strength was higher than the 1000°C and 1400°C samples. Mechanical properties of the SRBSN matrix composite were investigated at room temperature and elevated temperatures (up to 1400°C). The average room temperature values for matrix cracking stress and ultimate strength (in bend) were 651.1 and 713.2 MPa respectively, with corresponding Weibull moduli of 5.7 and 8.7. The stresses are comparable to similar monolithic silicon nitrides. Room temperature tensile matrix cracking and ultimate strength were 232MPa and 413MPa, lower than the bend test results, which were attributed to bending stresses in the sample, lowering the apparent failure stresses. The samples failed in a composite like manner (i.e. controlled rather than catastrophic failure), with a substantially higher woric of fracture than monolithic materials. The average matrix cracking and ultimate bend strength at 1200°C were 516MPa and 554MPa, dropping to 178MPa and 486MPa at 1400°C (the matrix cracking stress was indistinct at 1400°C due to plasticity). The creep and stress rupture properties at 1300°C were investigated in four point bend, using dead-weight loading. The creep rate was KH/s at a stress of 200MPa, lower than a hot pressed silicon nitride with MgO additive, and higher than a hot isostatically pressed Y2O2/SÍO2 additive silicon nitride. A cavitation creep mechanism was deduced from the stress exponent, which was >1. Failure by stress rupture did not have a lower limit, which is also associated with cavitation of the amorphous grain boundary phase.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:332596 |
| Date | January 1992 |
| Creators | Razzell, Anthony Gordon |
| Publisher | University of Warwick |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://wrap.warwick.ac.uk/110559/ |
Page generated in 0.0017 seconds