Ceramic armour must offer protection against armour piercing threats at low weight and affordable cost. As a possible means of improving armour, a range of SiC-B4C composites have been produced and characterised. The degree of contact between the two phases has been quantified and shown to have a strong effect on the densification and microstructure in these materials. This understanding has enabled independent variation of microstructural parameters which are normally interrelated. These were; porosity, SiC:B4C mass ratio, B4C distribution in a SiC matrix and SiC grain size distribution. To assess effects of each of these parameters on ballistic performance V50 testing was carried out, using 7.62 mm armour piercing rounds. The amount of porosity is shown to have a slight effect on V50 and a marked effect on scatter in V50. The pore size distribution is also shown to be important; across a range of pairs of materials with similar total pore volumes but differing pore size distributions, larger pores consistently give lower V50. SiC:B4C mass ratio does not seem to greatly affect V50, potentially allowing application specific cost/weight balances at constant protection level. B4C distribution has a strong effect. In general, for B4C features with diameters ranging from 1 m to 100 m, the coarser features performed better. Using coarse B4C particles in a SiC matrix, a V50 of approximately 980 ± 20 m s-1 at a density of 3.00 g cm-3 was achieved reproducibly. This material is preferred due to a combination of relatively lower cost, reduced density and repeatability. Knoop indentation has been used to derive possible merit indices which could potentially be used to rank ballistic materials. These includes analysis of failure probability of indents and the indentation size effect. A preliminary study indicates ballistic impacts may affect SiC polytype composition.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:685113 |
| Date | January 2016 |
| Creators | Williams, T. |
| Contributors | Yeomans, J. ; Smith, P. ; Hampson, C. ; Heaton, A. |
| Publisher | University of Surrey |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://epubs.surrey.ac.uk/810348/ |
Page generated in 0.0099 seconds