Hydroxyl terminated polybutadiene (HTPB) has been used as a rocket propellant binder which is required to be stored for at least twenty years. It is found that the excellent stress-strain characteristics of this propellant can be totally lost, during this long storage, due to the deterioration of the polybutadiene chains. As a result, the propellant can not stand the service loads, which may lead to a catastrophe. The study of the HTPB binder degradation, below 80°C, has been carried out by investigating the environmental factors and the changes which occur along the macromolecular chains. Results have shown that oxygen is the main factor which causes the crosslinking and chain scission reactions. The former is the predominant reaction and proceeds rapidly under oxygen sufficient environment. The unsaturation of polymer chain, which provides the desired physical properties to the binder, was lost with the increase in crosslink density. At the same time hydroperoxides were found to form and decompose along the polymer chains. Therefore, the deterioration of the binder results from the oxidation of polymer chains. Since the oxidation reaction occurred at higher rate than oxygen diffusion rate and oxygen diffusion rate is inversely proportional to the crosslink density, the binder, below the surface layer in a thick section container, could be naturally protected under an oxygen deficient condition for a long time. Investigation of the effectiveness of antioxidants in HTPB binder has shown that the efficiency of an antioxidant depends on its ability to scavenge radicals. Generally, aromatic amines are the most effective binder antioxidants. But when a peroxide decomposer is combined with an aromatic amine at the appropriate ratio, a synergistic effect is obtained, which gives the lowest binder gel increase rate.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:544714 |
| Date | January 1992 |
| Creators | Wang, Ting |
| Publisher | Aston University |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://publications.aston.ac.uk/9792/ |
Page generated in 0.0016 seconds