This thesis focuses on experimental characterization, understanding and modelling of nickel-based alloy 718, for a large range of loading conditions. Alloy 718 is the most widely used nickel-based superalloy, due to its high strength, high corrosion resistance and excellent mechanical properties at high temperatures. In this work, the mechanical behavior and microstructure evolution of this alloy during high strain rate deformation is investigated. Compression tests using a Split-Hopkinson pressure bar (SHPB) device were performed and the microstructure of the deformed sample was observed using optical microscope (OM) and scanning-electron microscope (SEM) coupled with electron back-scattered diffraction (EBSD) technique. The microstructural evolution according to the deformation conditions was characterized. For high deformation temperatures (1000 C and above), recrystallisation is identifed as the main deformation mechanism. A physics-based model was employed to simulate the deformation behavior of alloy 718. This type of models accounts for the microstructural mechanisms taking place during deformation. Knowledge about the deformation mechanisms of alloy 718, acquired experimentally and from literature, enables to formulate mathematically the microstructural phenomena governing the deformation behavior of the alloy. The proposed model includes the effects of strain hardening, grain boundary strengthening (Hall-Petch), solid solution strengthening, phonon and electron drag and recovery by dislocation glide and cross-slip. It is calibrated and validated using data obtained from mechanical tests, as well as values captured by the microstructural analysis. / H2020-MSCA-ITN-2017 grant agreement Nº764979 - ENABLE project
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ltu-83833 |
Date | January 2022 |
Creators | Moretti, Marie Anna |
Publisher | Luleå tekniska universitet, Hållfasthetslära, Luleå |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Licentiate thesis / Luleå University of Technology, 1402-1757 |
Page generated in 0.0017 seconds