The present thesis is focused on various methods of controlling electronic and geometrical structure of two-dimensional overlayers adsorbed on metal surfaces exemplified by graphene and hexagonal boron nitride (h-BN) grown on transition metal (TM) substrates. Combining synchrotron-radiation-based spectroscopic and various microscopic techniques with in situ sample preparation, we are able to trace the evolution of overlayer electronic and geometrical properties in overlayer/substrate systems, as well as changes of interfacial interaction in the latter.It is shown that hydrogen uptake by graphene/TM substrate strongly depends on the interfacial interaction between substrate and graphene, and on the geometrical structure of graphene. An energy gap opening in the electronic structure of graphene on TM substrates upon patterned adsorption of atomic species is demonstrated for the case of atomic oxygen adsorption on graphene/TM’s (≥0.35 eV for graphene/Ir(111)). A non-uniform character of adsorption in this case – patterned adsorption of atomic oxygen on graphene/Ir(111) due to the graphene height modulation is verified. A moderate oxidation of graphene/Ir(111) is found largely reversible. Contrary, oxidation of h-BN/Ir(111) results in replacing nitrogen atoms in the h-BN lattice with oxygen and irreversible formation of the B2O3 oxide-like structure. Pronounced hole doping (p-doping) of graphene upon intercalation with active agents – halogens or halides – is demonstrated, the level of the doping is dependent on the agent electronegativity. Hole concentration in graphene on Ir(111) intercalated with Cl and Br/AlBr3 is as high as ~2×1013 cm-2 and ~9×1012 cm-2, respectively. Unusual periodic wavy structures are reported for h-BN and graphene grown on Fe(110) surface. The h-BN monolayer on Fe(110) is periodically corrugated in a wavy fashion with an astonishing degree of long-range order, periodicity of 2.6 nm, and the corrugation amplitude of ~0.8 Å. The wavy pattern results from a strong chemical bonding between h-BN and Fe in combination with a lattice mismatch in either [11 ̅1] or [111 ̅] direction of the Fe(110) surface. Two primary orientations of h-BN on Fe(110) can be observed corresponding to the possible directions of lattice match between h-BN and Fe(110). Chemical vapor deposition (CVD) formation of graphene on iron is a formidable task because of high carbon solubility in iron and pronounced reactivity of the latter, favoring iron carbide formation. However, growth of graphene on epitaxial iron films can be realized by CVD at relatively low temperatures, and the formation of carbides can be avoided in excess of the carbon-containing precursors. The resulting graphene monolayer creates a periodically corrugated pattern on Fe(110): it is modulated in one dimension forming long waves with a period of ~4 nm parallel to the [001] direction of the substrate, with an additional height modulation along the wave crests. The novel 1D templates based on h-BN and graphene adsorbed on iron can possibly find an application in 1D nanopatterning. The possibility for growing high-quality graphene on iron substrate can be useful for the low-cost industrial-scale graphene production.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-194089 |
| Date | January 2013 |
| Creators | Vinogradov, Nikolay |
| Publisher | Uppsala universitet, Institutionen för fysik och astronomi, Uppsala |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1651-6214 ; 1019 |
Page generated in 0.0027 seconds