Orientador : Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T00:32:05Z (GMT). No. of bitstreams: 1
Cunha_MarciaReginaBernardida_M.pdf: 2234174 bytes, checksum: d5064ae556f27764bd71a1f2aca5f61e (MD5)
Previous issue date: 2001 / Resumo: O objetivo deste estudo foi avaliar a resistência de união à tração de sistemas adesivos dentinários convencionais e autocondicionantes aos 10 minutos e 24 horas pós-polimerização. Superfícies dentinárias planas foram preparadas nas faces superfícies vestibulares de 120 incisivos inferiores bovinos e sobre as quais foi delimitada a área de união de 4mm de diâmetro com fita adesiva. Nos grupos citados foram aplicados os seguintes sistemas adesivos seguidos da aplicação da resina composta Z 100: Grupo A e B - ScotchBond Multi-Uso Plus; Grupos C e D - Single Bond; Grupos E e F- Clearfil Liner Bond 2Ve Grupos G e H - Clearfil SE Bond. Nos Grupos A, B, C e D foi efetuado condicionamento com ácido fosfórico a 35% sobre a dentina por 15 segundos, seguida da lavagem e remoção do excesso de água. Um cilindro de resina composta foi posicionado sobre a área de união delimitada e fotoativado por 20 segundos em três pontos da interface para a realização do ensaio de tração, que foi conduzido após 10 minutos da união para os Grupos A, C, E e G. Os grupos B, D, F e H foram armazenados em água destilada a 37°C e o teste foi realizado após 24 horas em máquina de ensaio universal Instron com velocidade de 0,5mm/minuto, após o qual, o padrão de fratura foi observado sob Microscopia Eletrônica de Varredura. Os resultados foram submetidos à análise de variância e teste de Tukey (p< 0,05). Os resultados do ensaio de tração expressos em MPa foram: Grupo A- 7,69 +/- 1,40; Grupo B- 7,86 +/- 2,66; Grupo C- 8,56 +/- 2,97, Grupo D- 7,99 +/- 2,12; Grupo E 11,46 +/- 1,96; Grupo F- 12,97 +/- 2,86, Grupo G-11 ,73 +/- 3,01 e Grupo H- 13,04 +/-
3,57. Não houve diferença estatística significativa entre 10 minutos e 24 horas (p<O,05) para todos os grupos testados e os sistemas adesivos autocondicionantes foram estatisticamente superiores aos demais sistemas adesivos (p<O,05). O padrão de fratura predominante para os grupos de ScotchBond Multi-Uso e Single Bond foi coesivo no adesivo! Camada híbrida e nos grupos dos sistemas autocondicionantes foi coesiva em dentina. Os sistemas adesivos convencionais ScotchBond Multi-Uso e Single Bond, e os sistemas autocondicionantes Clearfil Liner Bond 2V e Clearfil SE Bond, apresentaram zonas de interdifusão resina! dentina com características morfológicas distintas, tanto em relação à espessura quanto na formação dos prolongamentos resinosos decorrentes da penetração do adesivo nos túbulos dentinários / Abstract: The purpose of this study was to evaluate the tensile bond strength of conventional dentin adhesive systems and self-etching primers at 10 minute and 24 hours. Flat dentin surfaces were prepared on labial surface of 120 bovine lower incisor teeth and a 4-mm-diameter bonding area was demarcated on each prepared surface with adhesive vinyl tape. In the following groups were applied the dentin systems and the composite resin Z 100: Groups A and B ¿ ScotchBond Multi-Purpose Plus and Z 100; Groups C and O - Single Bond; Groups E and F Clearfil Liner Bond 2V and Groups G and H - Clearfil SE Bond. In the groups A, B, C and O ali dentin was etched with 35% phosphoric acid, washed and the excess of water was removed. A resin composite rod was positioned on the bonding area and cured for 20 s at the three points of the interface to perform the tensile bond strength (TBS). The TBS was tested at 10 minute to groups A, C, E and G. The groups B, O, F and H were stored in distilled water at 37°C and the TBS was performed after 24 h. An Instron testing machine was used with a cross-head speed of 0,5 mm/min for the tensile test. After the TBS, the fracture pattern was observed by SEM. The results were analysed by ANOVA and Tukey's test (p<0,05). The TBS results expressed by MPa were: Group A- 7.69 +/- 1.40; Group B 7.86+/- 2.66; Group C- 8.56+/- 2.97, Group 0- 7.99+/- 2.12; Group E- 11.46+/- 1.96; Group F- 12.97 +/- 2.86, Group G-11.73 +/-3.01 and Group H- 13.04 +/- 3.57. There was no statistically significant difference among the 10 min and 24h groups. The more frequently fracture pattern was cohesive on the adhesive system for the A,B, C and o; and the Groups E, F, G and H showed cohesive fracture of dentin. The TBS of ali dentin bonding systems were similar at 10 min and 24 h and the self etching primers showed the highest values of TBS. The conventional adhesive systems, ScotchBond Multi-Use Plus and Single Bond, and the self etching primers, Clearfil Liner Bond 2V and Clearfil SE Bond, showed distinct morphological characteristics at resin dentin interdifusion zones about their thickness and resin tags created because of the infiltration of the adhesive resin into the dentin tubules / Mestrado / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288184 |
| Date | 19 February 2001 |
| Creators | Cunha, Marcia Regina Bernardi da |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Grande, Rosa Helena Miranda, Giannini, Marcelo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 78p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds