Orientador: Marcela Rocha de Oliveira Carrilho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T10:43:41Z (GMT). No. of bitstreams: 1
Malacarne-Zanon_Juliana_D.pdf: 9128347 bytes, checksum: 0fea8a055f819faabf3edb9b08ea04de (MD5)
Previous issue date: 2009 / Resumo: Este estudo, composto por três trabalhos, avaliou o efeito de diferentes tipos e concentrações de solventes orgânicos no grau de conversão (DC) e na permeabilidade de diferentes sistemas adesivos. No primeiro estudo, o DC de cinco adesivos experimentais de composição hidrófila/hidrófoba conhecida (R1<R2<R3<R4<R5), contendo 5%p/p ou 15%p/p etanol, assim como a sorção (WS), a solubilidade (SL) e a cinética de difusão da água (D) nos polímeros obtidos foram mensurados. No segundo estudo, a WS, a SL e a nanoinfiltração de prata (NN) em adesivos experimentais (R2, R3 e R5), polimerizados na presença de 15%p/p etanol ou 15%p/p acetona, foram avaliados após 7 dias (7d) e 6 meses (6m) de armazenamento. No terceiro estudo, foi avaliada a NN em sete adesivos comerciais, formulados com diferentes tipos e concentrações de solventes, para serem aplicados ao substrato dental com diferente número de passos clínicos. Todos os espécimes foram confeccionados em matriz metálica (0,8mm x 5,8mm), aplicando-se 80s de fotoativação a 650mW/cm2. O DC foi determinado por espectroscopia de infra-vermelho. Para o cálculo de WS, SL e D, os espécimes foram tratados de acordo com as normas da ISO 4049, exceto para os tempos de aferição das massas úmidas, que foram obtidos sequencialmente durante os 7 primeiros dias de armazenagem em água e após 6 meses. Para avaliação da nanoinfiltração, os espécimes foram infiltrados com nitrato de prata amoniacal, conforme protocolo de nanoinfiltração (Tay et al., 2002), exceto pelo tempo que os espécimes permaneceram na solução de nitrato de prata (48 h). Em seguida, os mesmos foram preparados para observação em microscópio eletrônico de varredura. Os valores obtidos de DC, WS, SL e D foram submetidos à análise de variância e, em seguida, ao teste de Tukey (a=0,05). A presença de etanol aumentou o DC de todas as resinas avaliadas, especialmente as mais hidrófobas R1 e R2 (p<0,05). A WS, a SL e o D dos adesivos experimentais aumentaram com a hidrofilia. Em geral, as resinas contendo 15% de solvente exibiram maior WS, SL e D que suas correspondentes não-solvatadas ou contendo 5% de solvente (p<0,05). Não foram encontradas diferenças significativas entre os tipos de solventes presentes (p>0,05). Diferenças significativas entre os tempos de avaliação de WS, de SL e de NN, em geral, foram encontradas para os espécimes mais hidrófilos (p<0,05). Os componentes menos hidrófilos dos sistemas adesivos indicados para serem aplicados utilizando-se maior número de etapas clínicas mostraram menor NN que os sistemas adesivos "simplificados". Adesivos hidrófilos apresentaram diferentes permeabilidades em solução aquosa. Os mais hidrófilos, contendo maiores concentrações de solventes orgânicos, são mais permeáveis e, consequentemente, mais susceptíveis à degradação ao longo do tempo. / Abstract: This study evaluated the effect of different solvent types and concentrations on the degree of conversion (DC) and permeability of different adhesive systems. In the first study, the DC of five experimental adhesives of known hydrophilicity based on their solubility parameters (R1<R2<R3<R4<R5), added with 5 wt% or 15 wt% ethanol, were evaluated. Additionally, water sorption (WS), solubility (SL) and diffusion coefficient of water (D) through the polymerized materials were also assessed. In the second work, the WS, SL and nanoleakage (NN) in model adhesives (R2, R3 e R5), polymerized in the presence of 15 wt% ethanol or 15 wt% acetone, were evaluated after 7 days (7d) and 6 months (6m) of water storage. In the third work, it was assessed the NN in seven commercial adhesive systems, formulated with different solvent types and concentrations, to be applied on dentin under different clinical approaches. All specimens were produced on teflon molds (0.8mm X 5.8mm), with 80 s of photoactivation, under 650 mmW/cm2. The DC was determined by infra-red spectroscopy. For WS, SL and D evaluations, specimens were treated according to ISO 4049, except for the times of m2 measurements, which were collected successively during the first 7 days of storage in water, and, then, after 6 months. For NN, specimens were stored in silver nitrate solution, according to the protocol reported by Tay et al. (2002), and then prepared for scanning electron microscopy evaluation. Values of DC, WS, SL and D were analyzed by ANOVA and Tukey's test (a=0,05). Ethanol addition increased the DC of all tested resins, but specially of the most hydrophobic ones, R1 and R2 (p<0.05). Permeability increased with the hydrophilicity of resin blends. In general, solvated resins exhibited significantly higher permeability than their correspondent neat versions (p<0.05). The only exceptions were R1 and R5, the least and the most hydrophilic adhesives respectively. Both exhibited similar WS values for neat and solvated versions (p>0.05). There were no significant differences when compared both solvents (p>0.05). Differences in WS, SL and NN, attributable to different times of water storage, were found for neat and solvated versions of R5. NN in the less hydrophilic components of commercial adhesive systems, indicated to be applied on dentin under multiple steps, were less evident than that observed in "simplified" adhesives. Based on the limitation of this study, it was concluded that more hydrophilic and solvated adhesives are more permeable to fluids diffusion and more vulnerable to water degradation effects over time. / Doutorado / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289848 |
| Date | 13 August 2018 |
| Creators | Malacarne-Zanon, Juliana |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Carrilho, Marcela Rocha de Oliveira, Wang, Linda, Garcia, Fernanda Cristina Pimentel, Goes, Mario Fernando de, Cunha, Leonardo Gonçalves |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 83 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds