With the growing trend of construction, the demand for building materials is growing steadily. Porous concrete is widely used in the building industry, that makes efforts to discount production and simultaneously save the environment. The aim of this thesis is to develop high-quality porous concrete by using alternative raw materials as a substitute for silicate sand. As a possible substitute were chosen: Silica masonry, foundry sand and fireclay boulders. The influence of two key parameters - the specific surface (130, 240 and 350 m2·kg-1) and the amount of silica sand substitution (10, 30 and 50 %) were monitored. Two autoclaving modes (7 and 12 hours of isothermal durations at 190 ° C) were tested. Based on the physico-mechanical and mineralogical characteristics of the porous concrete composites was chosen the ideal surface area of 240 m2·kg-1 and time of isothermal endurance was determined at 7 hours (temperature 190 ° C, pressure 1,4 MPa). From the optimal intentions were created samples with a macroporous structure, using an aluminum powder. Physical-mechanical properties and microstructural analysis (XRD, SEM) were subsequently determined on the samples. Ideal recipes were proposed with 50% sand substitution of fireclay boulders and 10% substitution of foundry sand. This was due to a 10% higher compressive strenght and an increase of the coefficient of constructiveness, compared to the reference sample.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:392332 |
| Date | January 2019 |
| Creators | Kostura, Patrik |
| Contributors | Janovský, Radek, Drochytka, Rostislav |
| Publisher | Vysoké učení technické v Brně. Fakulta stavební |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0049 seconds