Submitted by Ivone Costa (mivone@ufpa.br) on 2018-05-21T15:13:06Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_AvaliacaoDurabilidadeConcretos.pdf: 2178948 bytes, checksum: 9c47b0fa1f4b2c1164b582da2af1785b (MD5) / Approved for entry into archive by Ivone Costa (mivone@ufpa.br) on 2018-05-21T15:13:31Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_AvaliacaoDurabilidadeConcretos.pdf: 2178948 bytes, checksum: 9c47b0fa1f4b2c1164b582da2af1785b (MD5) / Made available in DSpace on 2018-05-21T15:13:31Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_AvaliacaoDurabilidadeConcretos.pdf: 2178948 bytes, checksum: 9c47b0fa1f4b2c1164b582da2af1785b (MD5)
Previous issue date: 2016-02-05 / A geração de resíduos de construção civil (RCC), no Brasil e no mundo são de
grandes proporções. Porém, o seu reaproveitamento não se dá na mesma
medida em que são gerados pela construção civil, soma-se a isso, a
necessidade de encontrar soluções para o depósito em aterros destes resíduos,
a insustentabilidade do consumo de recursos naturais, onde jazidas já
apresentam sinais de escassez de agregados. Logo, a utilização da cerâmica
vermelha como agregado para concreto traz consigo a consciência de
cooperação ambiental e sustentabilidade. Neste cenário, onde a bibliografia
ainda se encontra escassa com relação às propriedades de durabilidade do
concreto com este tipo de agregado, este trabalho teve como objetivo melhorar e
difundir o conhecimento a respeito deste resíduo na construção civil. Para isso,
foram produzidas misturas com relação água/cimento de 0.45; 0.55 e 0.65, onde,
o agregado miúdo natural foi substituído pelo agregado miúdo cerâmico em 0%,
12,5% e 25%, e cada porcentagem foi submetida às taxas de pré-molhagem de
40%, 60% e 80%. Posteriormente, foi avaliada a durabilidade dos concretos
produzidos com agregado miúdo cerâmico (AMC), através de ensaios de
absorção por capilaridade, carbonatação, resistividade elétrica e penetração de
íons cloretos. Com os resultados obtidos, pode-se concluir que o abatimento foi
satisfatório na maioria das misturas, e em relação à durabilidade, de modo geral,
todas as misturas com agregado reciclado cerâmico apresentaram maior
durabilidade que as de referência, principalmente nas misturas com 25% AMC.
As taxas de pré-molhagem mostraram-se eficientes na maioria das misturas,
mostrando satisfatória influência nos resultados finais em todos os ensaios
realizados. Portanto, conseguiu-se mostrar grande viabilidade da utilização deste
resíduo no concreto, melhorando o seu desempenho. / The generation of waste from civil construction (WCC) in Brazil and in the world
are of great proportions. However, its reuse does not occur in the same
proportions that are generated by construction, is added to this, the need to find
solutions for the landfilling of these wastes, unsustainable consumption of natural
resources, where deposits already present signals aggregate shortage.
Therefore, the use of red ceramic as recycled aggregate, reduces costs for the
production of concrete, brings awareness of environmental cooperation and
sustainability. In this scenario, the literature is still scarce in relation to the
concrete durability properties for this kind of aggregate. Thus, this study aimed to
improve and disseminate knowledge about these waste in construction. To this
end, mixtures were made with water / cement ratio of 0.45; 0.55 and 0.65, where
the aggregate has been replaced by natural fine ceramic aggregate in 0%,
12.5% and 25%, each percentage was subjected to pre-wetting rate of 40%, 60%
and 80%. Subsequently, the durability of concrete produced with fine ceramic
aggregate (FCA) was evaluated through capillary absorption, carbonation,
electrical resistivity and chloride ion penetration. With the results obtained it can
be concluded that the slump test was satisfactory in most mixtures, with respect
to durability, in general, all mixtures with ceramic recycled aggregate had higher
durability than the reference, especially in mixtures with 25% AMC. Pre-wetting
rates were effective in most mixtures, showing satisfactory influence on the final
results in all tests. So it managed to show great feasibility of using this waste in
concrete, improving their performance.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/9879 |
| Date | 05 February 2016 |
| Creators | MORAES, Ruan Fabrício Gonçalves |
| Contributors | SOUZA, Paulo Sérgio Lima |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Civil, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | 1 CD ROM, reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds