Experiments were conducted to investigate the potential of using a quench and self-tempering heat treatment process with AISI 1117 steel to satisfy the mechanical properties of ASTM A 706 rebar. A series of quenching tests were performed and the resulting microstructure and mechanical properties studied using optical microscopy, microhardness measurement, and tensile tests. The presence of martensite throughout the samples contributed to the enhanced strength and strain-hardening ratio (tensile to yield strength) of the material. The experimental results showed that AISI 1117 is capable of meeting the ASTM standard. In addition to the experiments, a computer model using the finite difference method and incorporating heat transfer and microstructure evolution was developed to assist in future optimization of the heat treatment process.
Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/29466 |
Date | 11 August 2011 |
Creators | Allen, Matthew |
Contributors | Wang, Zhirui |
Source Sets | University of Toronto |
Language | en_ca |
Detected Language | English |
Type | Thesis |
Page generated in 0.0016 seconds