Three aluminium alloys from AA3003 series modified by zirconium were pre- pared by twin-roll casting. The role of composition, heat treatment and deforma- tion by cold-rolling or equal channel angular pressing on evolution of microstruc- ture and mechanical properties were studied. High density of α-Al(Mn,Fe)Si pre- cipitates formed during annealing between 300 ◦ C and 500 ◦ C. Coherent Al3Zr particles precipitated during annealing at 450 ◦ C with slow heating rate. Recrys- tallization resistance of deformed alloys was enhanced by either Al3Zr precipitates formed before deformation or by α-Al(Mn,Fe)Si particles nucleating simultane- ously with recrystallization. 1
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:338095 |
Date | January 2014 |
Creators | Poková, Michaela |
Contributors | Cieslar, Miroslav, Karlík, Miroslav, Kruml, Tomáš |
Source Sets | Czech ETDs |
Language | English |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0014 seconds