Novel open-framework germanates and vanadoborates, which are constructed from typical types of clusters, have been synthesized based on different strategies. The crystal structures are solved by using single crystal X-ray diffraction (SXRD) technique or by combined techniques. Additionally, the structures of two open-framework materials, PKU-3 and PKU-16, are determined from nano-sized crystals by rotation electron diffraction (RED) combined with powder X-ray diffraction (PXRD). This thesis serves as an introduction to synthesis of open-framework germanates and vanadoborates based on different design strategies. Two germanates are obtained; SU-74 is achieved by employing a novel structure directing agent (SDA), SUT-8 is achieved by assembling the novel structure building units (SBUs) of Co@Ge14 with the introduction of cobalt ions in the synthesis. Four strategies are successfully used in construction of open-framework vanadoborates: using metal-oxo polyhedra as the linkages in SUT-6; applying the scale chemistry approach in SUT-7; employing metal-organic complexes as the linkages in SUT-12, SUT-13, SUT-14; and introducing covalent bond organic linkages into SUT-10 and SUT-11. Single crystal X-ray diffraction is used to conduct the structure determination in combination with other techniques. Furthermore, the structures of two open-framework materials, an aluminoborate PKU-3 and a germanosilicate PKU-16, are solved from nano-sized crystals using RED data. The structures are further confirmed by Rietveld refinement against PXRD data. The advantages of the RED techniques are demonstrated in two aspects. In PKU-3, the presence of seriously preferred orientation and light elements in the structure makes it difficult for structure determination by PXRD, but it is easier by RED. In PKU-16, the RED technique is used to determine its structure from the as-synthesized multi-phasic sample containing nano-sized crystals. After the structure of PKU-16 has been solved, the synthesis of this interesting phase can be optimized and pure PKU-16 can be obtained. Keywords: Open-framework, germanates, vanadoborates, aluminoborates, germanosilicates, crystal structure, hydrothermal synthesis, single crystal X-ray diffraction, rotation electron diffraction, powder X-ray diffraction
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:su-106853 |
| Date | January 2014 |
| Creators | Chen, Hong |
| Publisher | Stockholms universitet, Institutionen för material- och miljökemi (MMK), Stockholm : Department of Materials and Environmental Chemistry (MMK), Stockholm Univeristy |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds