An investigation of the microstructure-mechanical property relationships for gray cast iron and a vintage ASTM A7 steel are presented herein. Gray cast iron was shown to have a moderate sensitivity to strain rate and a large disparity in behavior between compression, tension, and torsion. ASTM A7 steel was shown to behave in a more complex manor with the strain rate sensitivity having a negative relationship in tension and positive relationship in compression and torsion, the tensile stress-state producing the highest stress response, and the material producing a higher stress response when exposed to elevated temperatures. The counterintuitive behavior observed in A7 steel was attributed to dynamic strain aging. The Mississippi State University Internal State Variable Plasticity-Damage model was updated to accurately capture negative strain rate sensitivity and DSA embrittlement by developing kinematic, thermodynamic, and kinetic constitutive relationships for dynamic strain aging. A parametric study was performed to elucidate the behavior of the new internal state variable for dynamic strain aging. Gray cast iron was successfully calibrated to a pre-DSA version of the plasticity-damage model and A7 steel was successfully calibrated to the updated plasticity-damage model.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-3781 |
| Date | 06 May 2017 |
| Creators | Brauer, Shane A |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.0024 seconds