A Ce:YAG-doped glass phosphor layer instead of conventional Ce:YAG-doped silicone phosphor layer as phosphor-converted white-light emitting diodes (PC-WLEDs) is demonstrated. The advantage of employing doped glass encapsulation in high power PC-WLEDs could be explained the material property of glass transition temperature of 750¢J was higher than silicone of 150¢J.
The lumen degradation, chromaticity shift, color temperature change, transmittance, and fluorescence spectrum in glass and silicone based high-power PC-WLEDs under thermal aging at 150¢J, 200¢J, and 250¢J is compared and presented. Under highest temperature of 250¢J, the glass and silicone encapsulation base d PC-WLEDs exhibited 8.15% and 38.85% in lumen loss, 1.07 and 7.32 in chromaticity shift, 856 K and 3666 K in color temperature change, 4.21% and 28.1% in transmittance loss, respectively. However, the excitation spectrum altered as slight as emission spectrum before and after experiments.
After aging test, the mean-time-to-failure (MTTF) evaluation of glass and silicone encapsulation materials for PC-WLEDs in accelerated thermal tests is also compared and presented by the using of Weibull distribution and Arrhenius equation. The MTTF of PC-WLEDs is defined the lumen decayed to 90%. The results showed that the glass as encapsulation material of PC-WLEDs exhibited higher MTTF than the silicone encapsulation by about 4.81, 5.92, and 7.53 times in lumen loss at 150¢J, 200¢J, and 250¢J, respectively.
The results of the lumen loss, chromaticity shift, and MTTF investigations demonstrated that the thermal-stability performance of the glass based PC-WLEDs were better than silicone based PC-WLEDs at 150¢J, 200¢J, and 250¢J. A better thermal stability phosphor layer of glass as encapsulation material may be beneficial to the many applications where the LED modules with high power and high reliability are demanded.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0804111-182558 |
| Date | 04 August 2011 |
| Creators | Liou, Jyun-Sian |
| Contributors | Wood-Hi Cheng, Cho-Hua Kuang, Chin-Ping Yu, Wen-Hou Lan, Chun-Chin Tsai |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0804111-182558 |
| Rights | user_define, Copyright information available at source archive |
Page generated in 0.0014 seconds