Poly(1,4-diethynylbenzene) ( -conjugated polymer) was prepared as an insoluble polymer network via chain coordination polymerization of 1,4-diethynylbezene catalyzed with [Rh(NBD)acac] complex. Thermodynamic properties and acid-base characteristics of the prepared poly(1,4-diethynylbenzene) were studied by means of Inverse Gas Chromatography (IGC) in the temperature range 80-100 řC. Retention data of selected testing substances were used to determine the Gibbs energy of sorption, the sorption enthalpy and their acid-base and disperse parts as well as the disperse contribution to the surface energy and parameters of KA, KD, ANHPS and DNHPS quantifying the acid-base character of the studied polymer. The results showed that poly(1,4-diethynylbenzene) interacted more efficiently with Lewis bases than with Lewis acids. The values of experimental sorption enthalpy were used for the determination of the parameters KA and KD. Values of these parameters classify poly(1,4-diethynylbenzene) as the material with a slightly acid character. This conclusion is further supported by the results of H. P. Schreiber method based on the application of ANHPS and DNHPS parameters for the evaluation of the acid-base properties of the material. The infrared spectroscopy proved that poly(1,4-diethynylbenzene) contained...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:297162 |
| Date | January 2011 |
| Creators | Petrášová, Sabina |
| Contributors | Sedláček, Jan, Pacáková, Věra |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0041 seconds