Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2014. / Made available in DSpace on 2015-09-08T04:03:45Z (GMT). No. of bitstreams: 1
334110.pdf: 8407341 bytes, checksum: 77d5842e7695e5505c7efc9a1deef622 (MD5)
Previous issue date: 2014 / Esta tese foi dividida em duas etapas. Na primeira etapa foram investigados aspectos sobre a cinética de austenitização na zona crítica de ferros nodulares com diferentes matrizes iniciais (bruta de fundição, austenítica, martensítica, perlítica, ausferrítica e ferrítica). Na segunda etapa foram apresentados dados referentes as propriedades mecânicas de ADI duais, proveniente das matrizes iniciais citadas acima. Primeiramente, foram obtidas e caracterizadas as amostras com as matrizes iniciais e foi realizada a escolha a temperatura de austenitização na zona crítica, 795°C. Esta temperatura foi determinada por método experimental e utilizando amostra inicialmente ferrítica. Para compreender a cinética de transformação, um primeiro grupo de amostras (com diferentes microestruturas iniciais) foi submetido tratamento isotérmico de austenitização na zona crítica, após diferentes tempos de austenitização as amostras foram resfriadas em água a temperatura ambiente. Todas as amostras desta etapa passaram por quantificação de fases, medidas de dureza e microdureza. Para a coleta de dados referentes a propriedades mecânicas, um segundo grupo de amostras (já usinadas e também com diferentes microestruturas iniciais) foi submetido a tratamento isotérmico de austenitização na zona crítica, em banho de sal, seguido de austêmpera a 350°C por 2h. Na primeira etapa do trabalho as amostras com matrizes iniciais bruta de fundição, austenítica e martensítica apresentaram cinética de transformações (para martensita) muito lentas. No entanto, na segunda etapa do trabalho, para as mesmas amostras iniciais (bruta de fundição e martensíticas), este comportamento foi mais rápido. Foi possível identificar, a presença de grafitas secundárias em algumas microestruturas resultantes deste trabalho, além de carbonetos não dissolvidos, mesmo após 12h de tratamento isotérmico. Amostras inicialmente ausferrítica e martensítica, na segunda etapa do trabalho, apresentaram melhor distribuição/homogeneização das fases (ferrita e ausferrita) na microestrutura final. As amostras inicialmente martensíticas e ausferríticas foram as que apresentaram valores de propriedades mecânicas superiores aos requisitados pela norma ASTM A897. Na presente tese, foi possível observar como ADI duais são extremamente sensíveis a temperatura e ao meio de tratamento térmico, causando variações na cinética de transformação, fração volumétrica de ferrita que consequentemente influência nos valores referentes as propriedades mecânicas.<br> / Abstract : This thesis has been divided into two steps. In the first stage aspects of the kinetics of austenitization were investigated in intercritical zone of ductile iron with different initial matrices (as casting, austenitic, martensitic, pearlitic, ferritic and ausferritic). In the second stage datas were submitted the mechanical properties of ADI dual, from the initial matrices mentioned above. Fist, were obtained and characterized the samples with the initial matrices. After, the choice was made to austenitization temperature in the critical zone, 795 ° C. This temperature was determined by experimental method and using initially ferritic sample. For the understanding of the kinetics of transformation a first group of samples (with different initial microstructure) was submitted to isothermal treatment in the intercritical zone austenitization followed (after different times), water quenching to room temperature. All samples have been had the measures of phase, hardness and microhardness. A second group of samples (machined and with different initial microstructures) was submitted to isothermal treatment in the intercritical zone in salt bath followed by austempering at 350 °C for 2 h to collect data for mechanical properties. In the first stage of this work, as casting, austenitic and martensitic initially samples exhibited kinetics of transformations (to martensite) very slow. However, in the second stage, for the same initial samples (as casting and martensitic), this behavior was different. It was possible to identify the presence of secondary graphite in some microstructures resulting from this work, and undissolved carbides, even after 12h of isothermal treatment. In the second stage of this work, ausferritics and martensitics initially samples showed better distribution/homogenization of the phases ferrite and ausferrite in the final microstructure. The martensitic and ausferríticas initially samples showed the superior values of the mechanical properties required by ASTM A897. In this thesis, it was possible to observe how the ADI dual are extremely sensitive to temperature and to kind of the heat treatment, causing variations in the kinetics of transformation, ferrite volume fraction that consequently influences the mechanical properties values.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/134759 |
| Date | January 2014 |
| Creators | Lopes, Clarissa Lussoli |
| Contributors | Universidade Federal de Santa Catarina, Bernardini, Pedro Amedeo Nannetti, Guesser, Wilson Luiz |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 194 p.| il., grafs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds