O objetivo deste estudo foi avaliar a Influência da associação de catalisadores químicos junto a diferentes sistemas adesivos autocondicionantes e cimentos resinosos de dupla polimerização, na cimentação de pinos pré-fabricados de fibra de vidro, quanto a sua resistência ao cisalhamento por extrusão - push out, seu grau de conversão e nanoinfiltração. Foram utilizadas trinta raízes bovinas extraídas, que tiveram seus canais obturados com guta-percha termoplastificada, divididas em três grupos: G1 - Adper SE Plus /Rely X ARC; G2- Adper SE Plus / Catalisador Scotchbond + Rely X ARC ; G3- Clearfil SE Bond / ED Primer + Panavia F. Após a cimentação dos pinos foram obtidas fatias das raízes, com 1mm de espessura, dos terços cervical (C), médio (M) e apical (A). O ensaio de resistência ao cisalhamento por extrusão foi realizado em máquina de ensaio universal EMIC D500 com carga de 100KN à velocidade de 1,0 mm/min, até o deslocamento do pino. Os dados obtidos no ensaio foram tabulados e submetidos à análise estatística. A análise de variância a dois critérios mostrou que apenas os fatores grupo e profundidade foram significativos, não sendo significativa a sua interação. O resultado do teste de Tukey (ρ≥0,05), para o fator grupo, mostrou que a menor média de resistência ao cisalhamento por extrusão foi obtida pelo grupo 3, que apresentou diferença estatística significativa para os grupos 1 e 2 que não diferiram entre si. Para o fator Profundidade a maior média foi obtida no terço cervical que apresentou diferença estatística significativa para os terços médio e apical que não diferiram entre si: A análise do grau de conversão foi feita após vinte e quatro horas e os fatores estudados foram os cimentos resinosos Panavia F e Rely X ARC e os catalisadores químicos ED Primer e Catalisador Scotchbond, na forma incorporada ou aplicada superficialmente aos cimentos, formando 10 grupos experimentais. Para o grau de conversão, o teste de Tukey mostrou que o catalisador químico não aumentou o grau de conversão do RelyX ARC, já para o Panavia F, este aumentou significativamente seu grau de conversão. Quanto a análise em MEV da nanoinfiltração para o fator grupo, o resultado do teste de Tukey (ρ≥0,05) mostrou que a maior média foi obtida pelo grupo 3 que apresentou diferença estatística significativa para os grupos 1 e 2, que não diferiram entre si. Para o fator Profundidade a maior média foi obtida no terço apical que apresentou diferença estatística significativa para o terço cervical, que não diferiu do terço médio. Conclusões: 1- A associação de catalisadores químicos não aumentou a resistência ao cisalhamento por extrusão dos pinos de fibra de vidro. 2- O cimento Panavia F é dependente de catalisador aumentar o grau de conversão. 3- A associação de catalisadores químicos não foi capaz de alterar o padrão da camada híbrida, representado pela nanoinfiltração. 4- A nanoinfiltração está associada inversamente ao grau de conversão dos sistemas de cimentação, o que contribui negativamente para a resistência adesiva de pinos de fibra de vidro. / The aim of this study was to evaluate the influence of catalyst solutions association with different self-etching adhesive systems and dual-cured resin luting agents used in prefabricated fiberglass posts cementation on the push-out bond strength test, degree of conversion and nanoleakage. Thirty extracted bovine roots were endodontically treated with thermoplastic gutta-percha and divided in three groups G1- Adper SE Plus /RelyX ARC; G2- Adper SE Plus / Scotchbond Catalyst + RelyX ARC; G3- Clearfil SE Bond / ED Primer + Panavia F. After post cementation, roots were sectioned into 1mm thick slices of cervical (C), middle (M) and apical(A) regions. Push-out tests were performed at a cross-head speed of 1,0 mm/min using a universal EMIC D500 testing machine applying 100KN load until the post dislodgment. The analysis of variance based on two criteria showed that only the factors group and depth were significant, their interaction was not significant. The Tukey's test (ρ ≥ 0.05) result for the factor group showed that the lowest average was obtained by the group 3, which showed significant difference from groups 1 and 2, that did not differ. The highest average for the depth factor, was obtained in the cervical third, which was statistically different from the middle and apical thirds that did not differ. The degree of conversion analysis was made after twenty-four hours and the studied factors were the Panavia F and Rely X ARC resin cements and ED Primer and Scotchbond chemical catalysts as incorporated or surface applied to the cement, forming 10 groups. For the degree of conversion, the Tukeys test showed that chemical catalyst did not increase the degree of conversion of RelyX ARC, but significantly increased the degree of conversion of Panavia F. The result of Tukey's test (ρ ≥ 0.05) of SEM analysis of nanoleakage for the group factor showed that the highest average was obtained by the group 3, statistically different from groups 1 and 2, that did not differ. For the depth factor, the highest average was obtained in the apical third, statistically different from the cervical third, which did not differ from the middle third. Conclusions: 1- The catalyst solutions association has not increased push-out bond strength of prefabricated fiberglass post. 2- Panavia F cement is dependent of catalyst solutions association to increase its degree of conversion. 3- The catalyst solutions association was not able to change the hybrid layer pattern, represented by nanolekeage; 3- Nanolekeage is inversely associated with the degree of conversion of the luting system, which contributes negatively to the bond strength of fiberglass posts.
| Identifer | oai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:UERJ:oai:www.bdtd.uerj.br:1496 |
| Date | 08 February 2010 |
| Creators | Angela Alexandre Meira Dias |
| Contributors | Hélio Rodrigues Sampaio Filho, Mauro Sayão de Miranda, Zilda Maria Castro de Carvalho, Vicente de Paulo Aragão Saboia, Marcos de Oliveira Barceleiro, Luís Alexandre Maffei Sartini Paulillo |
| Publisher | Universidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Odontologia, UERJ, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds