The diploma thesis studies composite of PP and filler particle. As a particle filler was used commercially available CaCO3 (SOCAL 31). The submitted thesis had a goal to find new approaches and technologies of filler surface treatment in order to improve properties of composite materials. The plasma discharge behind static pressure was used for the surface treatment of the fillers. These fillers were afterwards analyzed by using of sedimentation analysis, turbidimetry, infra-red spectroscopy (FT-IR), X-ray diffraction analysis (XRD), scan electron microscopy (SEM), transmission electron microscopy and particle size distribution by laser diffraction. The composites with various volume parts of the fillers were prepared in PIB and studied by short-time tests. Furthermore, the influence of an adhesive layer on fracture mechanical properties of prepared composite was study. Regarding to experimental demand, there was not possible to realize long-term mechanical properties.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216822 |
| Date | January 2012 |
| Creators | Dombková, Julie |
| Contributors | Krčma, František, Nezbedová, Eva |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds