High strain rate plastic deformation of metals results in the formation of localized zones of severe shear strain known as adiabatic shear bands (ASBs), which are a precursor to shear failure. The formation of ASBs in a high-strength low alloy steel, namely AISI 4340, was examined based on prior heat treatments (using different austenization and tempering temperatures), testing temperatures, and impact strain rates in order to map out grain size and grain deformation behaviour during the formation of ASBs. In the current experimental investigation, ASB formation was shown to be a microstructural phenomenon which depends on microstructural properties such as grain size, shape, orientation, and distribution of phases and hard particles—all controlled by the heat treatment process. Each grain is unique and its material properties are heterogeneous (based on its size, shape, and the complexity of the microstructure within the grain). Using measurements of grain size at various heat treatments as well as dynamic stress-strain data, a finite element model was developed using Matlab and explicit dynamic software LSDYNA to simulate the microstructural deformation of grains during the formation of ASBs. The model simulates the geometrical grain microstructure of steel in 2D using the Voronoi Tessellation algorithm and takes into account grain size, shape, orientation, and microstructural material property inhomogeneity between the grains and grain boundaries. The model takes advantage of the Smooth Particle Hydrodynamics (SPH) meshless method to simulate highly localized deformation as well as the Johnson-Cook Plasticity material model for defining the behavior of the steel at various heat treatments under high strain rate deformation.The Grain Model provides a superior representation of the kinematics of ASB formation on the microstructural level, based on grain size, shape and orientation. It is able to simulate the microstructural mechanism of ASB formation and grain refinement in AISI 4340 steel, more accurately and realistically than traditional macroscopic models, for a wide range of heat treatment and testing conditions.
| Identifer | oai:union.ndltd.org:MANITOBA/oai:mspace.lib.umanitoba.ca:1993/30072 |
| Date | 02 December 2014 |
| Creators | Polyzois, Ioannis |
| Contributors | Bassim, Nabil (Mechanical Engineering), Luo, Yunhua (Mechanical Engineering) Telichev, Igor (Mechanical Engineering) Shalaby, Ahmed (Civil Engineering) Wang, Zhirui (Materials Science and Technology, University of Toronto) |
| Source Sets | University of Manitoba Canada |
| Detected Language | English |
Page generated in 0.0023 seconds