The pursuit of high quality, large area graphene has been a major research focus of contemporary materials science research, in the wake of the discovery of the multitude of exceptional properties exhibited by the material. The DPhil project was undertaken with the objective of developing an understanding of the growth of large graphene sheets by chemical vapour deposition (CVD), and also in the subsequent characterisation of their material properties. By conducting atmospheric pressure CVD growth at high methane flow rates, it was found that few-layered graphene (FLG) could be deposited on a copper catalyst. It is demonstrated that the self-limiting property of a copper catalyst is not universal to all deposition conditions, and shown that FLG grows in a terrace-like configuration. In depth transmission electron microscopy (TEM) studies were carried out on FLG. By selective image reconstruction from the inverse power spectrum of the TEM images, it was possible to elucidate the inter-grain connectivity of few-layer graphenes. It was determined that there were two possible inter-grain configurations possible; specifically an overlap of graphene layers or a discrete atomic bonding edge. The perturbation of the few-layer structure when subject to an out of plane distortion was found to incur a shift in the conventional AB-Bernal stacking of FLG. By utilising the aberration corrected TEM (AC-TEM) at Oxford it was possible to resolve atomic detail in CVD synthesised monolayer films, including atomic bond rotations and vacancies. The use of a high current density at low accelerating voltage (80 kV) was demonstrated to allow for the controlled defect creation in graphene sheets. This permitted the creation of monovacancies and iron doped vacancy complexes suitable for further study. The behaviour of these two defect types under electron beam irradiation was subsequently studied.
Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:588413 |
Date | January 2013 |
Creators | Robertson, Alexander William |
Contributors | Warner, Jamie H.; Briggs, Andrew |
Publisher | University of Oxford |
Source Sets | Ethos UK |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Source | http://ora.ox.ac.uk/objects/uuid:aee750dd-41b8-4462-9efa-4e89e06e0ed7 |
Page generated in 0.0015 seconds