000829587.pdf: 1025900 bytes, checksum: caf14058fe0da647247682c65c55da7c (MD5) / O concreto de alto desempenho (CAD) possui uma densa microestrutura que lhe proporciona ao mesmo, alta resistência e redução de sua permeabilidade. Com isso, apresenta alta durabilidade, sendo maior que a do concreto convencional. Esse fato mostra que a utilização deste concreto está crescendo rapidamente em diversas obras. Este produto tem como base a cinza de bagaço de cana-de-açúcar (CBC), que possui grande potencial para ser utilizada como aditivo mineral em concretos, uma vez que é composta por dióxido de silício. A partir dessas afirmações, esta pesquisa apresenta a finalidade de analisar o desempenho da adição de CBC sem sofrer o processo de moagem, na fabricação do concreto de alto desempenho. Para tanto, foi feita a substituição de CBC na proporção de 5%, 10%, 15% e 20%, sendo esta substituída na quantidade de agregado miúdo em massa. Os ensaios realizados foram: absorção, módulo de elasticidade, resistência à compressão e resistência à tração por compressão diametral para as idades de 7, 28, 60 e 90 dias. Chegou-se, portanto, à conclusão que o CAD com CBC de substituição em 20% de agregado miúdo em massa foi o que obteve o melhor desempenho, por isso foi o traço escolhido para os ensaios de durabilidade, tais como: resistência ao ataque químico, absorção por capilaridade, frente à penetração de cloretos, ensaio de abrasão/erosão e permeabilidade à água. Assim, os resultados obtidos nos ensaios foram comparados aos mesmos ensaios realizados com o concreto referência, ou seja, CAD sem nenhuma adição. A partir daí, observou-se que, em determinados casos, o CAD com adição de CBC apresentou resultados iguais ou até mesmo superiores ao do concreto referência / The high performance concrete (CAD) has a dense microstructure which provides the same, high strength and reduced permeability. With this, it has high durability, being greater than that of conventional concrete. This fact makes their use is growing rapidly in several works. Regarding bagasse ash cane sugar (CBC), this has great potential to be used as a mineral additive for concrete, since it is composed of silicon dioxide. Thus, this research has the purpose of analyzing the performance of the addition of CBC without undergoing milling, manufacturing of high performance concrete. Replacement of was which is substituted in the proportion of 5%, 10%, 15% and 20%, the amount of aggregate in massa. Os tests were performed: absorption, modulus of elasticity, compressive strength and tensile strength by diametrical compression to the ages of 7, 28, 60 and 90 days. Was reached, so the conclusion that CAD with CBC replacement in 20% of aggregate mass, was what had the best performance, so it was chosen for durability testing trait and which were the following: resistance to chemical attack, wicking, across the penetration of chlorides abrasion test / erosion and water permeability. The results obtained in the tests were compared to tests performed with the same reference concrete, that is, without addition CAD, showing in some cases, the addition of CAD with CBC showed equal or even superior results to the reference concrete
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/124098 |
| Date | 18 August 2014 |
| Creators | Fernandes, Sérgio Eduardo [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Tashima, Mauro Mitsuuchi [UNESP], Akasaki, Jorge Luís [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 96 f. : il. color. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |
Page generated in 0.0071 seconds