The mesoporous materials Al-MCM-41 produced from kaolin, low cost raw material, by means of hydrothermal acid treatment route, has shown potential for being used as adsorbent in removal process of methylene blue. The process of synthesis of Al-MCM-41 is based on calcination of kaolin, dealumination by acid treatment, hydrothermal synthesis and extraction of the surfactant. The characterization of de obtained mesoporous material was carried out by techniques such as: X-ray diffraction, vibrational spectroscopy in the infrared, 29Si and 27Al nuclear magnetic resonance in the solid state, scanning electron microscopy, transmission electron microscopy and N2 adsorption/desorption. The X-ray diffraction at low angles allowed the determination of the cell parameter, which was 4.02 nm. The analyses of scanning and transmission electron microscopy revealed important morphological properties of the synthesized material. N2 adsorption/desorption showed a BET specific surface area of 1,303 m2 g-1, pore volume of 1.23 cm3 g-1 and average diameter of 2.45 nm. PZC measurements showed a pHPZC of 2.69. The adsorption of methylene blue by Al-MCM-41 adsorbent showed high kinetic and high adsorption capacity, with values around 316 mg g-1. / O material mesoporoso Al-MCM-41 produzido a partir de caulim, matÃria-prima de baixo custo, por meio de rota hidrotÃrmica com tratamento Ãcido, mostrou-se promissor para ser usado como adsorvente do corante azul de metileno. O processo de sÃntese da Al-MCM-41 Ã baseado na calcinaÃÃo do caulim, desaluminizaÃÃo por tratamento Ãcido, sÃntese hidrotÃrmica e eliminaÃÃo do surfactante. A caracterizaÃÃo do material mesoporoso foi realizada por meio de tÃcnicas como: difraÃÃo de raios-X, espectroscopia vibracional na regiÃo do infravermelho, ressonÃncia magnÃtica nuclear no estado sÃlido de 29Si e 27Al, microscopia eletrÃnica de varredura, microscopia eletrÃnica de transmissÃo e adsorÃÃo de N2. A anÃlise de difraÃÃo de raios-X em baixo Ãngulo da Al-MCM-41 permitiu a determinaÃÃo do parÃmetro de cÃlula que apresentou valor de 4,02 nm. As anÃlises de microscopia eletrÃnica de varredura e de transmissÃo revelaram importantes propriedades morfolÃgicas do material sintetizado. Utilizando as medidas de adsorÃÃo e desorÃÃo de gÃs N2 a Ãrea superficial especÃfica BET da Al-MCM-41 apresentou valor 1.303 m2 g-1, com um volume de poros de 1,23 cm3 g-1 e diÃmetro mÃdio de 2,45 nm. O teste do PZC determinou um pHPZC de 2,69. Os testes de adsorÃÃo do azul de metileno pelo adsorvente Al-MCM-41 mostraram que o mesmo apresenta alta capacidade de adsorÃÃo com valores em torno de 316 mg g-1.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:10471 |
| Date | 14 October 2015 |
| Creators | EvÃnia Carvalho dos Santos |
| Contributors | Adonay Rodrigues Loiola, Cristiane Pinto Oliveira, Francisco Wagner de Sousa |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em QuÃmica, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0038 seconds