Aluminium alloys with Si as the major alloying element form a class of material providing the most significant part of all casting manufactured materials. These alloys have a wide range of applications in the automotive and aerospace industries due to an excellent combination of castability and mechanical properties, as well as good corrosion resistance and wear resistivity. Additions of minor alloying elements such as Cu and Mg improve the mechanical properties and make the alloy responsive to heat treatment. The aim of this work is studying the role of size and morphology of microstructural constituents (e.g SDAS, Si-particles and intermetalics) on mechanical properties of Al-Si based casting alloy at room temperatures up to 500 ºC. The cooling rate controls the secondary dendrite arm spacing (SDAS), size and distribution of secondary phases. As SDAS becomes smaller, porosity and second phase constituents are dispersed more finely and evenly. This refinement of the microstructure leads to substantial improvement in tensile properties (e.g. Rm and εF). Addition of about 280 ppm Sr to EN AC- 46000 alloy yields fully modified Si-particles (from coarse plates to fine fibres) regardless of the cooling conditions. Depression in eutectic growth temperature as a result of Sr addition was found to be strongly correlated to the level of modification irrespective of coarseness of microstructure. Modification treatment can improve elongation to failure to a great extent as long as the intermetallic compounds are refined in size. Above 300 ºC, tensile strength, Rp0.2 and Rm, of EN AC-46000 alloys are dramatically degraded while the ductility was increased. The fine microstructure (SDAS 10 μm) has superior Rm and ductility compared to the coarse microstructure (SDAS 25 μm) at all test temperature (from room to 500 ºC). Concentration of solutes (e.g. Cu and Mg) in the dendrites increases at 300 ºC and above where Rp0.2 monotonically decreased. The brittleness of the alloy below 300 ºC was related to accumulation of a high volume fraction damaged particles such as Cu- Fe-bearing phases and Si-particles. The initiation rate of damage in the coarse particles was significantly higher, which enhances the probability of failure and decreasing both Rm and εF compared to the fine microstructure. A physically-based model was adapted, improved and validated in order to predict the flow stress behaviour of EN AC- 46000 cast alloys at room temperature up to 400 ºC for various microstructures. The temperature dependant variables of the model were quite well correlated to the underlying physics of the material
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hj-26805 |
| Date | January 2015 |
| Creators | Zamani, Mohammadreza |
| Publisher | Tekniska Högskolan, Högskolan i Jönköping, JTH. Forskningsmiljö Material och tillverkning – Gjutning, Tekniska Högskolan, Högskolan i Jönköping, JTH, Maskinteknik, Jönköping : Jönköping University, School of Engineering |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | JTH Dissertation Series ; 07 |
Page generated in 0.0026 seconds