This thesis is focused on the principles of behavior of shrinkage reducing agents (SRA) in alkali-activated materials based on blast furnace slag. The main focus of this work is selecting the most suitable admixture based on experiments, by which will be achieved through minimal shrinkage and will have negative effect on the properties of alkali-activated blast furnace slag at the same time. In experimental section of this work, the surface tension as individual additives as their mixtures with pore solution were measured primarily. Then the testing samples composed of blast furnace slag, water glass and addition of SRA were prepared. Of these samples was measured shrinkage and weight loss. Moreover, their mechanical properties such as flexural and compressive strength were monitored. Next, the beginning and the end of solidification was studied using the Vicat device and last but not least workability. The hydration process of alkali-activated materials with SRA was measured calorimetrically. Finally the microstructure in prepared samples was observed using scanning electron microscopy (SEM-EDS) and the total porosity was determined by mercury porosimeter.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:295703 |
| Date | January 2017 |
| Creators | Komosná, Kateřina |
| Contributors | Bartoníčková, Eva, Kalina, Lukáš |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds