The thermodynamic properties of the copper-manganese system were determined by the measurement of the vapour pressure of manganese tagged with Mn⁵⁴, using the Knudsen effusion method.
Manganese shows a positive deviation from Raoult's law over the entire composition range. Copper, although showing a strong positive departure from Raoult's law at low copper content, shows a slight negative departure in copper-rich compositions. The negative departure, which can be associated with an affinity of copper for manganese is greatest at compositions of about 35% manganese.
The behavior of both copper and manganese is much more ideal at lower manganese compositions.
The ideal behaviour of the manganese in the alloys of low manganese content and the affinity of copper for manganese at about 35% manganese appear to corroborate Myers interpretation of the electronic configurations of copper and manganese in this system. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/40114 |
| Date | January 1958 |
| Creators | Peters, Bruno Frank |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0024 seconds