Metalografia, análise de oxigênio e nitrogênio e teste de dureza vickers dos materiais de fixação interna usados no esqueleto craniofacial / Metallography, oxygenand nitrogen composition and vickers hardness test of internal fixation materials used in the craniofacial skeleton

Orientador: Roger William Fernandes Moreira / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T14:42:14Z (GMT). No. of bitstreams: 1
Mendes_MarceloBrenoMeneses_M.pdf: 5487742 bytes, checksum: e1f89d1bc60060a4c330175efda763d9 (MD5)
Previous issue date: 2012 / Resumo: Este trabalho tem o objetivo de analisar, através de metalografia, análise da composição de gases oxigênio e nitrogênio e por meio de teste de dureza Vickers, 4 marcas de material de fixação interna utilizadas na cirurgia buco-maxilo-facial (grupo I = Leibinger; grupo II = Tóride; grupo III = Engimplan; grupo IV = Medartis). Inicialmente, foram confeccionados três corpos de prova com segmento de placa de três elos e três corpos de prova com parafusos, para cada grupo. Realizou-se preparação e análise metalográfica, de acordo com as normas da ASTM E3-95. Em seguida, as amostras foram submetidas ao teste de dureza Vickers, obedecendo às normas da ASTM E92. Após, foi realizado análise da composição de gases oxigênio e nitrogênio, com um segmento de elo de placa e um parafuso, para cada grupo. Os dados foram submetidos à análise de variância e teste de Tukey para comparação dos resultados. Todas as etapas dos processos foram registradas e fotografadas. De acordo com os resultados encontrados, os parafusos apresentaram maior dureza, em comparação com as placas. Entre estas, as placas do grupo IV apresentaram os grãos de maiores dimensão. A análise da composição dos gases revelou que todos os grupos atendem às normas ASTM / Abstract: This study aims to analyze 04 brands of internal fixation material, used in oral and maxillofacial surgery (Leibinger = group I; Tóride = group II; Engimplan = group III; Medartis = group IV) by metallography, analyzing the composition of gaseous oxygen (O) and nitrogen (N), and Vickers hardness testing. Initially,three specimens with three rings of the plate and three specimens with screws were made for each group. The preparation of the specimens was performed to metallographic analysis, attending the ASTM E3-95 standards. And then the samples were submitted to Vickers hardness test, according to the ASTM E92 standards. Thereafter, the composition analysis of the contents of O and N in all groups was performed with a ring of the plate and a screw for each group. Data were submitted to ANOVA and Tukey's test for result comparison. All steps of the process were recorded and photographed. According to the results, the screws had higher hardness, compared to the plates. Including, the plates of group IV showed the largest grain size. The analysis of the gas composition showed that all groups followed ASTM standards / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288766
Date21 August 2018
CreatorsMendes, Marcelo Breno Meneses, 1984-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Moreira, Roger William Fernandes, 1971-, Araúo, Marcelo Marota, Filho, Francisco Wagner Vasconcelos Freire
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format70 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0027 seconds