This thesis explores the posibility of using of foundry filter ash for production of inorganic composite materials, that could be used primary in the construction industry. The thesis is divided into theoretical and experimental section, where theoretical section contain literature review of used materials and the experimental section summarizes the results of laboratory tests performed on tested mixture based on portland and alumina cement with various content of foundry filter ash. For comparison was also used another foundry waste - foundry sand. Prepared test bodies with dimension of 40 x 40x 160 mm was subjected to mechanical strength tests and the influence of amount of foundry waste on the strenght of the prepared mixtures was monitored. Next the thesis deals with possibilities of alkaline activation of foundry waste, where sodium water glass, sodium hydroxide and commercially supplied baucis L 160 component B were used as alkaline activator. These test mixtures were also subjected to mechanical strenght tests and the influence of amount of foundry waste on the strenght was observed too. The analysis of input materials were performed by XRF, TG – DTA – EGA and XRD powder diffraction methods. All strength tests were tested by testing equipment desttest 4310.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216871 |
Date | January 2012 |
Creators | Solik, Jaroslav |
Contributors | Šoukal, František, Opravil, Tomáš |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds