This thesis deals with refractory concrete binding system based on aluminous cement and phosphoric acid. The prepared refractory concretes were fired at 1 000 °C. Various effects on compressive strength of refractory concrete were studied. The influence of aluminous cement content and phosphoric acid content, the influence of various admixtures, the influence of plasticizers and the influence of time and method of sample storage were studied. Simultaneous thermogravimetry and differential thermal analysis of the basic unfired sample were performed. Finally, selected refractory concretes were fired at 110, 200, 400, 600, 800, 900, 1 000 and 1 100 °C. The compressive strength of these samples was measured and powder X ray diffraction analysis was performed. The compressive strength of refractory concretes under intermediate temperatures (800–1 100 °C) was most increased in samples with metakaolin and gray microsilica.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414129 |
| Date | January 2020 |
| Creators | Pavlík, Tomáš |
| Contributors | Švec, Jiří, Šiler, Pavel |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds