Studium pojivového systému pro žárobetony na bázi kyseliny fosforečné a hlinitanového cementu / The study of the refractory concrete binding system based on phosphoric acid and aluminous cement

This thesis deals with refractory concrete binding system based on aluminous cement and phosphoric acid. The prepared refractory concretes were fired at 1 000 °C. Various effects on compressive strength of refractory concrete were studied. The influence of aluminous cement content and phosphoric acid content, the influence of various admixtures, the influence of plasticizers and the influence of time and method of sample storage were studied. Simultaneous thermogravimetry and differential thermal analysis of the basic unfired sample were performed. Finally, selected refractory concretes were fired at 110, 200, 400, 600, 800, 900, 1 000 and 1 100 °C. The compressive strength of these samples was measured and powder X ray diffraction analysis was performed. The compressive strength of refractory concretes under intermediate temperatures (800–1 100 °C) was most increased in samples with metakaolin and gray microsilica.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414129
Date January 2020
CreatorsPavlík, Tomáš
ContributorsŠvec, Jiří, Šiler, Pavel
PublisherVysoké učení technické v Brně. Fakulta chemická
Source SetsCzech ETDs
LanguageCzech
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0018 seconds