Fatigue crack growth mechanisms in Al-Si-Mg alloys

Thesis (Ph. D.)--Worcester Polytechnic Institute. / Keywords: Microstructure; Elastic-Plastic Fracture Mechanics; Crack closure; A356; J-integral; Conventionally cast and SSM Al-Si-Mg alloys; Residual stress; Heat treatment; Fatigue crack growth mechanisms; Threshold stress intensity factor; Plastic zone; Paris law; Fracture toughness; Roughness. Includes bibliographical references.