Aluminum nitride (AlN) thin film is a promising material as buffer layer in GaN-based optoelectronic and electronic devices or as a substrate to fabricate Surface Acoustic Wave (SAW) and Film Bulk Acoustic wave Resonant (FBAR) devices in high frequency in wireless (>1GHz) communication technology. Aluminum nitride, thin film with the c-axis normal to the film is favored in a low energy deposition condition because it places the packed hexagonal basal plane parallel to the substrate surface. Grains of this orientation have a low surface energy which favors rapid growth in a columnar structure.
In this experiment r.f. dual ion beam sputtering (DIBS) system is used to prepare the AlN films on Si (100) substrate. Various processing variable were tested to deposit AlN films with desirable properties. After systematic testing, a high quality film with preferred c-axis orientation was grown successfully on Si (100) substrate with Al target under the process parameters of 700 ev energy flux; 55% N2 / (N2+Ar) ratio; 4X10 - 4 torr working pressure with no heating of substrate. The AlN target is also used. The results show the great sensitivity of the films to oxygen-containing environments. Only under low residual oxygen pressure, could aluminum nitride be grown well.
The deposited AlN thin film characteristic were studied by X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), Transmission Electron Microscopy (TEM), Secondary Ion Mass Spectrometry (SIMS) and Electron Spectroscopy for Chemical Analysis (ESCA).
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0715104-044714 |
Date | 15 July 2004 |
Creators | Chao, Chien-po |
Contributors | Der-shin Gan, none, Pouyan Shen |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0715104-044714 |
Rights | not_available, Copyright information available at source archive |
Page generated in 0.0011 seconds