The effects of quenching conditions, single-step and two-step aging treatments on the tensile properties of an AL-4.5%Cu-1.5%Mg alloy has been investigated. Results indicate that two distinctly different precipitates of GPB and S' form during aging. Single-step aging at 140°C , 160°C and 190°C indicated that 24 hours at 160°C produced optimum strength (67 ksi UTS). Two-step aging for 3 days at 140°C plus 190°C resulted in a slight increase in strength over single step aging at 190°C. Slow (oil) quenching as well as direct quenching improved the tensile properties when aged at 190°C. Reversion occurred slowly over the temperature range 250°C to 350°C.
| Identifer | oai:union.ndltd.org:ucf.edu/oai:stars.library.ucf.edu:rtd-1382 |
| Date | 01 January 1977 |
| Creators | Sulouff, Robert Earl |
| Publisher | Florida Technological University |
| Source Sets | University of Central Florida |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Retrospective Theses and Dissertations |
| Rights | Public Domain |
Page generated in 0.002 seconds