Magnetism of Nanocrystallized Amorphous Fe75B10Si15

Amorphous ribbons of alloy composition Fe75B10Si15 are cast by melt spinning and annealed to partially nanocrystalline states. The magnetic properties are investigated by VSM and MTGA. Structure is examined using XRD and SEM. Results obtained show nanostructured material with excellent soft magnetism in samples annealed at temperatures below the crystallization temperature as well as enhancement of magnetic hardness for annealing at high temperatures. This validates Herzer’s Random Anisotropy model of magnetism in nanostructured materials and provides basis for further inquiry into tweaking alloy compositions and/or manipulating annealing parameters. Also, increase of Curie temperature is noted with respect to increasing annealing temperatures arising from stress relaxation, validating a study on the relationship between the two.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-107191
Date January 2012
CreatorsChakraborty, Arnab
PublisherKTH, Materialvetenskap
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0018 seconds