O objetivo deste estudo foi avaliar parâmetros para o desenvolvimento de métodos visando à determinação elementar em alumina, cimento e quartzo por espectrometria de emissão óptica com plasma indutivamente acoplado (ICP OES) com amostragem de suspensão. Alguns elementos foram investigados como possíveis candidatos a padrões internos (PIs) Be, Dy, Gd, In, La, Sc, Y, Yb eTl. Amostras de material de referência certificado (CRM) de alumina (Alumina Reduction Grade 699), de cimento Portland (1889a Blended with Limestone e 1886a White Portland cement with low iron) do National Institute of Standard and Technology (NIST), e amostras de quartzo, cedidos pelo Departamento de Física da Universidade Federal de São Carlos (UFSCar), denominados T-4FI, T-2FI e T-4GR, foram utilizadas na otimização instrumental, no desenvolvimento e na avaliação da exatidão do método. Nanopartículas de sílica de alta pureza (Wacker HDK® T40), Wacker Chemie AG foram utilizadas no estudo de adsorção dos elementos e padrões internos como proposta de produção de material calibrante para a análise direta de sólidos. Para a escolha dos PIs foram construídos gráficos de correlação usando valores de potenciais de excitação, energias de ionização e temperaturas de fusão dos analitos e dos candidatos a PIs. Análise exploratória por agrupamentos hierárquicos (HCA) e análise dos componentes principais (PCA), também foram realizadas. A avaliação de desempenho do ICP OES foi feita em meio das suspensões das amostras a partir do estabelecimento de figuras de mérito como sensibilidade, robustez, seletividade e repetibilidade. Na otimização do foram considerados os parâmetros potência, vazão de nebulização e vazão de gás auxiliar. A determinação de Ca, Fe, Ga, Na, Si e Zn em alumina foi feita após dissolução em forno de micro-ondas com posterior precipitação do Al(III) com NH3. O uso de padrão interno foi essencial para a exatidão do método, com recuperações do CRM que variaram de 83 a 117%. Para a matriz cimento foram avaliados o efeito da concentração de ácido nítrico na extração dos analitos ( Al, Ca, Cr, Fe, K, Mg, Mn, Na, P, S, Si, Sr, Ti e Zn) e na adsorção dos elementos candidatos a PIs (Be, Sc, In, Dy). As determinações por suspensão e uso de padrão interno (exceto para Cr, S e Zn), com 0,5% v v-1 de HNO3, nebulizador Burgener e condições robustas do ICP geraram resultados com recuperações entre 68 e 119%. As determinações de Al, Ba, Cr, Fe, K, Li, Mg, Na, Sr e Ti em quartzo foram executadas com introdução de suspensão e ausência de padrão interno, usando condições do ICP similares àquelas adotadas na determinação elementar para matriz de cimento. Nesse caso as recuperações variaram de 90 a 107%. A adsorção dos analitos e padrões internos sobre as nanopartículas de sílica pode ser uma alternativa para a preparação de padrões de calibração quando se deseja realizar a introdução direta do material sólido em suspensão. / The aim of this study was to evaluate parameters for the development of methods for elements determination in alumina, cement and quartz by inductively coupled plasma optical emission spectrometry (ICP OES) with slurry sampling. Some elements were investigated as candidates for internal standards (ISs) Be, Dy, Gd, In, La, Sc, Y, Yb and Tl. Samples of certified reference material (CRM) of alumina (Alumina Reduction Grade - 699), Portland cement (blended with the 1889a and 1886a Limestone White Portland cement with low iron) from the National Institute of Standards and Technology (NIST), and quartz samples, suplied by the Department of Physics from Federal University of São Carlos (UFSCar), named T-4FI, T-2FI and T4GR were used to optimize instrumental, method development and accuracy evaluation of the method. Nanoparticles of high purity silica (Wacker HDK T40 ®), Wacker Chemie AG were used in the study adsorption of the analytes and internal standards as calibrating material for direct analysis of solids. Correlation graphs using excitation potentials, ionization energies and melting point temperatures were used for chosing the best ISs. Exploratory analysis using hierarchical cluster analysis (HCA) and principal component analysis (PCA) were also performed. Optimization of ICP OES was performed in aqueous and slurry samples to establishment figures of merit, such as sensitivity, robustness, selectivity and repeatability. In the optimization of ICP, power supply, nebulizer flow rate and auxiliary gas flow rate were considered. The determination of Ca, Fe, Ga, In, Si and Zn in alumina was made after decomposition in a microwave oven with subsequent precipitation of Al(III) with NH3 gas. The internal standard was essential to obtain the accuracy of the method, with recoveries of CRM analysis ranging from 83 to 117%. For the cement analysis was evaluated the effect of nitric acid concentration over analytes extraction (Al, Ca, Cr, Fe, K, Mg, Mn, Na, P, S, Si, Sr, Ti and Zn) and ISs candidate adsorption (Be, Sc, In and Dy). Determinations of the elements in cement slurry with the internal standard (except for Cr and Zn), with 0.5% v v-1 HNO3, nebulizer Burgener and robust conditions of ICP produced results with recoveries between 68 and 119%. The determinations of Al, Ba, Cr, Fe, K, Li, Mg, Na, Sr and Ti in quartz were performed with the slurry introduction and without of internal standard, using similar conditions of those adopted for cement matrix. In this case the recoveries ranged from 90 to 107% with addition and recovery test. The adsorption of the analytes and internal standards on silica nanoparticles could be an alternative for the preparation of calibration standards when considering performing the direct introduction of solid material.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-13102011-085326 |
| Date | 29 July 2011 |
| Creators | Alexandre Luiz de Souza |
| Contributors | Pedro Vitoriano de Oliveira, Lucio Angnes, Joaquim de Araujo Nobrega, Ana Rita de Araujo Nogueira, Fabio Rodrigo Piovezani Rocha |
| Publisher | Universidade de São Paulo, Química, USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0034 seconds