Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-06-10T19:03:35Z
No. of bitstreams: 1
UbiratanCorreiaSilva_TESE.pdf: 29378655 bytes, checksum: 1c6a0b8bc21d1601438ddbfc07854def (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-06-13T20:18:34Z (GMT) No. of bitstreams: 1
UbiratanCorreiaSilva_TESE.pdf: 29378655 bytes, checksum: 1c6a0b8bc21d1601438ddbfc07854def (MD5) / Made available in DSpace on 2016-06-13T20:18:34Z (GMT). No. of bitstreams: 1
UbiratanCorreiaSilva_TESE.pdf: 29378655 bytes, checksum: 1c6a0b8bc21d1601438ddbfc07854def (MD5)
Previous issue date: 2015-08-28 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico (CNPq) / Multicamadas magn?ticas s?o a base para a produ??o de dispositivos spintr?nicos e possuir
o dom?nio na produ??o de tais multicamadas ? fundamental para obter avan?os nesta ?rea, e
nos ?ltimos anos est? em destaque a produ??o de dispositivos spintr?nicos flex?veis. Devido
a essa tend?ncia, o objetivo do presente trabalho ? produzir multicamadas magn?ticas depositadas
em substrato flex?vel utilizando a t?cnica de Magnetron sputtering dc. Tr?s conjuntos
de amostras foram confeccionados. O primeiro conjunto, constitu?do de tricamadas do tipo
CoFe=Cu(t)=CoFe com diferentes espessuras do espa?ador met?lico. O Segundo conjunto,
composto por dois subgrupos de multicamadas CoFe=Cu com a presen?a do IrMn como buffer
layer ou cap layer. O terceiro conjunto, constitu?do por multicamadas de Permalloy (Py=Ta
e Py=Ag) em substrato da Kapton e substrato de vidro. Para a investiga??o das propriedades
magn?ticas, foram realizadas medidas de magnetometria de amostra vibrante, resson?ncia ferromagn?tica
e magnetoimped?ncia (MI). Todas executadas em temperatura ambiente e com
campo magn?tico aplicado sempre no plano da amostra. Para a an?lise estrutural, a t?cnica de
difra??o de raios-X foi usada. Os resultados das tricamadas mostraram a apresen?a de uma
anisotropia uniaxial, para a amostra com espa?ador de 4;2 nm. Para a multicamada com a presen?a
do IrMn entre a camada buffer e FM, os resultados das propriedades magn?ticas est?ticas
e din?micas apresentaram comportamento isotr?pico. Para a multicamada com a presen?a do
IrMn entre a camada FM e a cap layer, os resultados das propriedades magn?ticas est?ticas
apresentaram o comportamento magn?tico de uma estrutura tipo v?lvula de spin. Entretanto
houve uma diverg?ncia com resultados das medidas de resson?ncia ferromagn?tica, a qual foi
justificada devido ? contribui??o dos gr?os inst?veis e est?veis para a anisotropia rod?vel e anisotropia
de polariza??o (Exchange bias) na interface ferromagn?tica-antiferromagn?tica. Para
a terceira s?rie de amostras, os resultados apresentaram comportamentos semelhantes da MI
cujo espa?ador foi a prata (Ag), para ambos os substratos e varia??o significativa nas amostras
com o espa?ador por Ta onde foi poss?vel associar a varia??o da magnetoimped?ncia entre os
substratos de vidro e flex?vel, ao estresse compressivo na amostra de substrato flex?vel. / Magnetic multilayers are the support for the production of spintronic devices, representing
great possibilities for miniaturized electronics industry. having the control to produce devices
as well as their physical properties from simple multilayer films to highly complex at the atomic
scale is a fundamental need for progress in this area, in recent years has highlighted the
production of organic and flexible spintronic devices. Because of this trend, the objective of this work was to produce magnetic multilayers deposited on flexible substrate using magnetron sputtering dc technique. Three sets of samples were prepared. The first set composed of the trilayer type CoFe=Cu(t)=CoFe with different thickness of the metallic spacer. The second set consists of two multilayer subgroups, CoFe=Cu
in the presence of IrMn layer as a buffer and the next multilayer as cap layer. The third set
consisting of non-magnetostrictive multilayer permalloy (Py=Ta and Py=Ag) on flexible substrate
and glass. The magnetic properties, were investigated by magnetometry measurements,
ferromagnetic resonance and magnetoimpedance (MI), measurements were carried out at room
temperature with the magnetic field always applied on the sample plane. For structural analysis,
the diffraction X-ray was used. The results of the trilayer showed a high uniaxial anisotropy
field for the sample with a spacer of 4.2 nm. For the multilayer in the presence of IrMn layer as
the buffer, the study of static and dynamic magnetic properties showed isotropic behavior. For
the multilayer in the presence of IrMn layer as a cap, the results of static magnetic properties of
the magnetic behavior exhibited a spin valve structure type. However there was a disagreement
with results of ferromagnetic resonance measurements, which was justified by the contribution
of the unstable and stable grain to the rotatable anisotropy and Exchange bias in ferromagneticantiferromagnetic interface. The third serie of samples showed similar results behavior for the
MI Ag multilayers spacer in both substrates. There are also significant MI changes with the Ta
spacer, possible associated with the compressive stress on the flexible substrate sample.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/20691 |
Date | 28 August 2015 |
Creators | Silva, Ubiratan Correia |
Contributors | 03187557422, http://lattes.cnpq.br/0832037849525983, Gon?alves, Charlie Salvador, 00829954430, http://lattes.cnpq.br/9064755417050889, Torres, Marco Antonio Morales, 05225041752, http://lattes.cnpq.br/0091292234916055, Souza, Thatyara Freire de, 04603726457, http://lattes.cnpq.br/8483112335128610, Feitosa, Carlos Chesman de Ara?jo, Oliveira, Alexandre Barbosa de |
Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM F?SICA, UFRN, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds