Redox reactions and structure - properties relations in mixed alkali/alkaline earth glasses : - The role of antimony oxides during the fining process- A structural study of copper(I) and copper(II)

It is important to optimize glass compositions for their specific purpose but also for the efficiency of the production process, the manufacturing of glass. This will be beneficial economically and environmentally. Today many processes and glass compositions are already optimized, but due to more strict legislation on toxic elements and substances there must be changes in many glass compositions. One of these elements is antimony; the oxide is used as fining agent to obtain a bubble free glass within a reasonable process time. One aim with this thesis is to obtain a deeper understanding of the fining mechanism in 20R2O-10MO-70SiO2 (R=Na and/or K, M = Ca and/or Ba, Mg, Sr) glasses in order to minimise the amount of Sb2O3. Another intention is to study the structure of 20R2O-10CaO-70SiO2 (R = Na, K) with Cu2+ as probe ion and thus get a deeper knowledge of the surrounding glass matrix.  The optical basicity scale is used to determine the acid/base character of the different glass compositions.   Fining efficiency results showed a remarkable increase of the number of remaining bubbles when the glass contains either approximately equal amounts of Na and K or Ca and Ba, Mg or Sr. The much higher number of bubbles in the potassium containing glasses compared to the sodium containing is explained by the increase in viscosity, the increase in optical basicity and thus lower oxygen activity. The differences in the fining efficiency when altering alkaline earth ions cannot be explained by the optical basicity values, it seems to be a more complicated situation.   This thesis also reports maximum in Vickers hardness and packing density as well as minimum in glass transition temperature for the mixed alkali glasses. The mixed alkaline earth glasses do not exhibit any clear nonlinear behaviour. Raman spectroscopy measurements showed a variation in the network connectivity which has a clear relation to the optical basicity of the different glass compositions. The combination of UV-Vis-NIR and X-ray absorption spectroscopy measurements showed that the coordination sphere for Cu(II) is a tetragonal distorted octahedron with two elongated Cu-O bonds along the z axis. There were no trends in the degree of tetragonal distortion, thus it was about the same for all the investigated glass compositions. Cu(I) is found to be coordinated by two oxygen ligands in mainly linear coordination sphere, evidenced from X-ray absorption spectroscopy.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:lnu-46782
Date January 2015
CreatorsGrund Bäck, Lina
PublisherLinnéuniversitetet, Institutionen för byggd miljö och energiteknik (BET), Växjö
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationLinnaeus University Dissertations ; 231

Page generated in 0.0017 seconds