Complexity of quasicrystal approximants —The RECd6 and RE13(Zn/Cd)~58 systems

This thesis is focused on the synthesis and structural determination of a series of quasicrystal approximants in the RE13Zn~58 (RE = Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu), Ce13Cd~58 and RECd6 (RE = Tb, Ho, Er, Tm and Lu) systems. Structural studies were performed by single crystal X-ray diffraction methods. The RECd6 phases are 1/1 cubic approximants to the stable icosahedral quasicrystals. The structure of quasicrystals cannot be solved by conventional crystallography due to the lack of periodicity in three-dimensional space. On the other hand, quasicrystal approximants exhibit long-range order, which makes their structural determination possible by standard methods. Since they are believed to display the same local arrangement as the quasicrystals, the structures of the quasicrystal approximants play a key role in understanding quasicrystals. The RE13Zn~58 and Ce13Cd~58 quasicrystal approximants show measurable compositional variations coupled to subtle structural differences. The crystal structures are generally rather more complex than previously reported, and exhibit a number of different ordering and disordering modes.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:su-7203
Date January 2007
CreatorsPiao, ShuYing
PublisherStockholms universitet, Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi, Stockholm : Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds