Efeito de diferentes tempos e temperaturas de volatilização de solventes sobre o grau de conversão e as propriedades mecânicas de sistemas adesivos dentinários / Effect of different volatilization times and temperatures of solvents on degree of conversion and mechanical properties of dentin bonding systems

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T10:15:57Z (GMT). No. of bitstreams: 1
Araujo_LarissaSgarbosaNapoleaode_M.pdf: 3474527 bytes, checksum: 9bfdeda78eb0f2e753e727642f5d8c80 (MD5)
Previous issue date: 2011 / Resumo: O objetivo deste estudo foi avaliar a influência de diferentes tempos (5s, 10s, 20s) e temperaturas (±23º, ±40ºC) para volatilização de sistemas adesivos [Excite (EX) e Single Bond 2 (SB)] sobre o grau de conversão (GC), resistência coesiva (RC), módulo de elasticidade (ME) e resistência à flexão (RF). A fonte de luz LED - Elipar Free Light 2 foi utilizada para fotoativação das amostras por 20 s (1100 mw/ cm2). Para a análise da RC, RF e ME cada corpo de prova foi confeccionado a partir de uma matriz de silicone por adição em forma de barra (2x1x7mm). Sobre a matriz, foram dispensados 10 ?L de adesivo após receberem leve jato de ar com tempo e temperatura variando de acordo com cada grupo, e fotoativados por 20s. Para análise de RC (n=10), os corpos de prova foram fixados à Máquina de Ensaio com célula de carga de 200N, e para RF e ME (n=5) com carga de 50N, ambos realizados a 0,5mm/ min, até a ruptura da amostra. Para mensuração do GC (n=5) foram dispensados 3?L de adesivo sobre o cristal e utilizada espectroscopia de transmissão infravermelha de Fourier (FTIR) na faixa de 1665 a 1580 cm-1. Os dados foram submetidos a análise de variância 3 fatores e teste de Tukey (p< 0,05). Para EX e SB, a temperatura de ±40ºC resultou em maior RC em todos os tempos de volatilização. Os maiores valores de RC foram observados no tempo de 20s, seguidos dos tempos de 10s e 5s, respectivamente. Maiores valores de RC foram encontrados para o adesivo EX comparativamente ao SB. Para GC não houve diferença estatisticamente significante para EX entre as temperaturas e tempos de volatilização estudados. Para SB, maiores valores de GC foram obtidos com a temperatura de ±40ºC com exceção do grupo volatilizado por 20s, que não diferiu estatisticamente da temperatura de ±23ºC. EX apresentou maiores valores de GC que SB, independente de tempo e temperatura de volatilização. Com relação ao ME, para EX não houve diferença estatisticamente significante entre os tempos e as temperaturas de volatilização. Apenas para SB, a temperatura de ±40ºC promoveu aumento no ME e, entre os tempos de volatilização não houve diferença estatisticamente significante. De acordo com o resultado da análise da RF, para EX não foi observado efeito estatisticamente significante entre as temperaturas de volatilização estudadas. A volatilização à temperatura de ±40ºC de SB resultou em melhor desempenho na RF. Para tempo de volatilização, tanto para SB quanto para EX, independente da temperatura de volatilização, os tempos de 20 e 10s não diferiram estatisticamente entre si e foram maiores do que 5s. Os resultados deste estudo indicam que há uma superioridade do adesivo à base de etanol sobre os que associam etanol e água. De modo geral, a volatilização por 20s elevou o desempenho dos sistemas adesivos testados. A volatilização com altas temperaturas dos sistemas adesivos avaliados, elevou o GC bem como as propriedades mecânicas dos mesmos. O ar aquecido elevou a resistência coesiva dos adesivos à base de etanol / Abstract: The aim of this study was to evaluate the influence of different times (5s, 10s, 20s) and temperatures (±23º, ±40ºC) for volatilization of various adhesive systems [Excite (EX) and Single Bond 2 (SB)] on the degree of conversion (DC), cohesive strength (CS), modulus of elasticity (ME) and the flexural strenght (FS). The light curing unit Elipar Free Light 2- LED was used for curing the samples by 20s. For the analysis of CS, FS and ME each specimen was made from a silicone matrix addition with the stick format (2x1x7mm). On the matrix were dispensed 10 ?L of adhesive after receiving gentle air with time and temperature varying according to each group, and were cured for 20s. For analysis of CS (n=10), the specimens were fixed to the Testing Machine with a load cel of 200N, and for FS and ME (n= 5) with a load of 50N, both held at 0.5 mm/min until failure of the sample. For measurement of DC (n = 5), after volatilization, were dispensed 3 ?L of adhesive on the crystal and used Fourier Transform Infrared transmission Spectroscopy (FTIR) in the range from 1665 to 1580 cm-1. The data were subjected to three factors ANOVA and Tukey test (p <0.05). For EX and SB, the temperature of ± 40°C resulted in higher CS at all times of evaporation. The highest values of CS were observed in 20s, followed by times of 10s and 5s, respectively. Higher values of CS were found for the adhesive EX compared to SB. For GC there was no statistically significant difference for EX between the times and temperatures volatilization studied. For SB, higher values of DC were obtained with a temperature of ±40 ºC with the exception of the group volatilized of 20s, that did not differ from temperature of ±23ºC. EX presented higher values of DC followed by SB, regardless of time and temperature of volatilization. Regarding the ME, to EX, there was no statistically significant difference between the times and temperatures of volatilization. Just to SB, the temperature of ±40°C promoted an increase in the ME, and between times of volatilization there was no statistically significant difference. According to the outcome of the FS, for EX was not observed statistically significant effect between the temperatures of volatilization studied. The temperature of ± 40 ºC of SB resulted in better performance in FS. On the time of volatilization for both SB and EX, independent of volatilization temperature, the times of 20 and 10s did not differ statistically and were higher than 5s. The results of this study indicate that there is a superiority of ethanol-based adhesive on those where there is the association of ethanol and water. In general, the volatilization for 20s increased the performance of adhesive systems evaluated. Volatilization at high temperature adhesive systems based on water and ethanol, has raised its DC and the mechanical properties of them. The heated air increased CS of adhesives based on ethanol / Mestrado / Dentística / Mestre em Clínica Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289115
Date18 August 2018
CreatorsAraújo, Larissa Sgarbosa Napoleão de, 1984-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Marchi, Giselle Maria, 1970-, Santos, Paulo Henrique dos, Sinhoreti, Mário Alexandre Coelho
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format57 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds