Previous issue date: 2016-02-15 / Facepe / A grande demanda de cinza de algaroba gerada nas lavanderias pertencentes ao APL de
Pernambuco e sua constituição química prioritária de carbonato de cálcio, caracterizando seu
efeito filler, impulsionaram a verificação do comportamento do sistema cimentício quando da
substituição do cimento pela cinza nas argamassas de revestimento. O objetivo deste trabalho
é utilizar o resíduo, atualmente descartado no ambiente, em materiais cimentícios, de modo a
contribuir para o desenvolvimento sustentável, reduzindo o impacto produzido pelo
armazenamento e descarte inadequado. Além disso, pretende-se contribuir para a redução da
emissão de CO2 causada pelas indústrias cimenteiras e minimizar os custos dos produtos com
cimento Portland. Neste trabalho, foi avaliada a influência da substituição do cimento Portland
em diferentes porcentagens (0%, 5%, 10% e 20%) nas propriedades nos estados fresco e
endurecido das argamassas, aplicando no traço (1-X):2:X:9 (cimento: cal: cinza: areia), em
volume, comumente utilizado para emboço e argamassa de assentamento em obras da região.
A cinza foi caracterizada física e quimicamente. As propriedades analisadas no estado fresco
foram: reologia das argamassas (reometria de mistura, de cisalhamento e compressiva - squezze
flow), densidade de massa e teor de ar incorporado e aderência inicial das argamassas no
substrato; e no estado endurecido foram: resistência à tração por compressão diametral,
resistência potencial de aderência à tração, módulo de elasticidade dinâmico, porosidade e
permeabilidade. De acordo com os resultados obtidos nesta pesquisa, a presença da cinza
favoreceu, em todas as porcentagens estudadas, a redução no teor de água de amassamento,
mantendo a trabalhabilidade das argamassas. As argamassas com teores de 5% de cinza
preservam as propriedades do sistema compatíveis com as propriedades da argamassa de
referência. Porém, até 10% é possível a introdução deste resíduo, em substituição ao cimento,
sem prejuízos aos sistemas cimentícios, proporcionando alterações mínimas em relação à
argamassa de referência, sendo promissor o uso desse resíduo em materiais cimentícios. / There is a considerable production of algaroba wood ash in the laundries of the local productive
arrangement on the clothing industry in the Agreste Region of Pernambuco. It is possible to
apply it as filler due to its mainly chemical constitution as calcium carbonate. Based on these
facts, it was evaluated the mortars behaviour when cement is partial replaced by algaroba ashes.
This work objectives reuse this residue, currently discarded in the environment, in cementitious
materials. In this way, it contributes to the sustainable development by reducing the impact by
storage and improper disposal. Moreover, it is intended contributes to reducing CO2 emissions
caused by cement industries and minimize the costs of products with Portland cement. This
study investigates the influence of the gradual replacement of cement by algaroba ash (0%, 5%,
10% and 20%). It was evaluated the properties of mortars in fresh and hardened states. The mix
by volume (1-X):2:X:9 (cement, lime, ash, sand) was studied, taking into account that these
alternative mortars can be applied on regional building sites as rendering plaster and laying
mortar. The ashes were characterized physically and chemically. It was carried out in the fresh
state: rheology of mortars (mixture, compressive and shear rheometers - squeeze flow), mass
density, a content of entrained air and initial adherence of the mortars to the substrate; and in
the hardened state: diametrical traction, potential adherence, dynamic modulus of elasticity,
porosity and permeability. The results indicate that the presence of the ashes decreases the
quantity of mixing water required to keep the workability of the mortars, regardless the content
of cement replacement content by algaroba ash. The mortar with 5% ash content preserving
system properties compatible with the properties of the reference mortar. However, it is possible
to partial substitute the cement by algaroba ash until 10% in the studied mortars, when
comparing to the reference system, algaroba ashes are a promising material to incorporate in a
cementitious system.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/17150 |
| Date | 15 February 2016 |
| Creators | PIRES, Dannúbia Ribeiro |
| Contributors | http://lattes.cnpq.br/3109732203611868, NÓBREGA, Ana Cecília Vieira da, MARINHO, Erika Pinto |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Civil e Ambiental, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds