Previous issue date: 2016-02-26 / Neste trabalho, blendas de polietileno de alta densidade com polietileno linear de baixa densidade metalocênico, PEAD/m-PELBD, foram preparadas empregando uma extrusora dupla rosca, cônica, contrarotacional interpenetrante e os efeitos do tipo e do teor do m-PELBD nas propriedades de impacto e de tração foram estudados. A blenda PEAD/m-PELBD com melhor relação de propriedades, tenacidade/rigidez, foi modificada com argila montmorilonita organofílica comercial Cloisite 20A, nos teores de 1, 3, 5 e 10 pcr, visando à obtenção de um híbrido com propriedades comparáveis, particularmente, em processamento e tenacidade/rigidez, às da resina de PEAD importada, PEAD Dowlex IP–10262, utilizada para fabricação de embalagens injetadas para o envase e transporte de produtos químicos perigosos. De acordo com os resultados da caracterização mecânica (impacto e tração), ficou evidenciado que o tipo e o teor de m-PELBD influenciaram nestas propriedades. Dentre os m-PELBDs estudados, Flexus 7200 e Flexus 9200, o Flexus 7200 resultou na melhor relação de propriedades e dentre os teores avaliados (10, 17 e 25%), o teor de 17% foi mais efetivo. A blenda PEAD/17% m-PELBD, blenda 7217, apresentou resistência à tração no escoamento comparável a da resina importada; resistência ao impacto 57,7% superior e módulo elástico 23,6% inferior. Como a rigidez da blenda 7217 foi inferior à da resina importada, a mesma foi modificada com a argila Cloisite 20A. De acordo com os dados de difratometria de raios X (DRX), a incorporação da argila à blenda 7217, em todos os teores estudados, não resultou na formação de nanocompósitos. Apesar disso, as propriedades de cristalinidade (determinada por calorimetria exploratória diferencial – DSC) e de estabilidade térmica (determinada por termogravimetria - TGA) da blenda 7217 modificada com 10 pcr de argila (7217AO-10), foram superiores as da blenda pura. A resistência à tração foi mantida, a resistência ao impacto diminuiu e o módulo elástico aumentou, em relação a blenda pura. Em comparação com a resina importada, a resistência à tração do híbrido 7217AO-10 foi 8% superior, a resistência ao impacto foi 12% inferior e o módulo elástico 7% inferior. De forma geral, a blenda 7217, modificada com 10 pcr de argila, apresentou processabilidade e propriedades mecânicas comparáveis as da resina importada (PEAD Dowlex IP–10262). / Blends of high density polyethylene with metallocene linear low density polyethylene, HDPE/m-LLDPE, were prepared by melt compounding in a twin-screw extruder. The m-LLDPE type and content effects on impact and tensile properties were studied. According to the results, these parameters influenced the properties of m-LLDPE. The blend prepared with m-LLDPE Flexus 7200 with the 17% concentration (7217 blend) showed the best properties. However, their hardness was lower than the HDPE Dowlex IP-10262 resin, used for dangerous chemicals transport containers manufacture. The 7217 blend was modified with organophilic montmorillonite (Cloisite 20A organoclay). The diffraction X-ray data (XRD) showed that the 7217 blend modification, with organoclay, on all studied concentrations, did not result in nanocomposites. Nevertheless, the crystallinity properties (determined by differential scanning calorimetry – DSC) and thermal stability (determined by thermogravimetric analysis – TGA) of the 7217 blend, modified with 10 phr of organoclay (7217AO-10) were higher than the pure blend. In addition, the modified blend showed decreased impact resistance, increased elastic modulus and the same tensile strength. As compared to Dowlex IP-10262 HDPE, the tensile strength of 7217AO-10 hybrid was 8% higher, the impact strength was 12% lower and the elastic modulus was 7% lower. In general, the processability and mechanical properties of 7217 blend, modified with 10phr of Cloisite 20A, were similar to that HDPE Dowlex IP-10262. Therefore, this hybrid has great use potencial for dangerous chemicals transport containers manufacture, replacing the HDPE Dowlex IP-10262 resin.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1042 |
Date | 26 June 2018 |
Creators | NASCIMENTO, Uédson Alexandre do. |
Contributors | SILVA, Suédina Maria de Lima., ARAÚJO, Edcleide Maria., MELO, Tomás Jeferson Alves de., Andrade, Daniela de Lourdes A. C. S., BRAGA, Carla Ramalho Costa. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0101 seconds