Uticaj mikrostrukture na prelaznu temperaturu ADI materijala / Microstructure influence on ductile to brittle transition temperature of ADI materials

<p>U disertaciji je izvršena karakterizacija mikrostrukture i mehaničkih osobina<br />nelegiranog austemperovanogi nodularnog liva (ADI materijala), kao i uticaja<br />mikrostrukture na prelaznu temperaturu u intervalu od -196 do +100&deg;C.<br />Utvrđeno je da mehaničke osobine ADI-ja zavise od morfologije ausferitne<br />mikrostrukture i količine zadržanog austenita, tj. parametara austemperovanja.<br />Na osnovu mehaničkih osobina utvrđen je i opseg procesiranja u skladu sa<br />standardima ASTM, ISO i EN. Zaključeno je da prelazna temperatura ADI<br />materijala zavisi od količine i stabilnosti zadržanog austenita. U višem<br />temperaturnom opsegu (iznad cca. -25&deg;C) dominantna je količina zadržanog<br />austenita, dok na nižim temperaturama, stabilnost. Visoka obogaćenost<br />ugljenikom, stabilnog zadržanog austenita sprečava stvaranje martenzita na<br />niskim temperaturama, a time i pojavu krtosti kod ADI-ja.</p> / <p>The object of this thesis was to characterize microstructure and mechanical properties<br />of the unalloyed ADI material (Austempered Ductile Iron). In addition, the influence of<br />microstructure on the ductile to brittle transition temperature (DBTT) by Charpy impact<br />test in temperature interval from 196 to +100&deg;C has been studied. The all properties<br />obtained depend on the morphology of microstructure and the amount of retained<br />austenite, i.e. on the austempering parameters. According to the mechanical properties<br />and standard requirements (ASTM, ISO and EN) the processing window has been<br />proposed, also. It was found that DBTT is influenced by amount and stability of retained<br />austenite. In upper temperature range (above cca. 25&deg;C) the most influence factor on<br />DBTT is amount of retained austenite, while at the lower temperatures the stability is<br />more prominent. Stability of high carbon retained austenite at lower temperatures<br />prevents transformation to martensite and thus the embrittlement of ADI.</p>

Identiferoai:union.ndltd.org:uns.ac.rs/oai:CRISUNS:(BISIS)94932
Date10 July 2015
CreatorsRajnović Dragan
ContributorsŠiđanin Leposava, Gerić Katarina, Kakaš Damir, Burzić Zijah, Erić Cekić Olivera
PublisherUniverzitet u Novom Sadu, Fakultet tehničkih nauka u Novom Sadu, University of Novi Sad, Faculty of Technical Sciences at Novi Sad
Source SetsUniversity of Novi Sad
LanguageSerbian
Detected LanguageEnglish
TypePhD thesis