The aim of this dissertation work is the evaluation of the influence of nickel alloying on the structure and mechanical properties, both monotonic and dynamic, of nodular cast iron with ferritic and bainitic matrix. Two chock melts with 0.5 and 2.7 % Ni were used to study the nickel influence. The quantitative evaluation of structure of these melts using image analysis was done and basic tensile mechanical properties were determined. Subsequently, the time optimization of two-stage ferritic annealing and isothermal austempered heat treatment at 375 °C was performed with the aim to obtain optimal ferritic and bainitic structures with best static and dynamic mechanical properties. After ferritic annealing the nickel alloying contributes to substitution hardening of ferritic matrix which positively affects its strength and other mechanical properties. The higher nickel content in the bainitic structure causes the shift of phase transformation times to longer times which results in restricted production of small carbides and in bigger volume of retained austenite. These features were confirmed by observation in transmission electron microscope. Precise tensile and low cycle fatigue tests at temperatures 23 and – 45 °C were performed on the optimized structures of both nodular cast irons. As a result of the notch effect of graphite nodules, microplastic deformation of both nodular cast irons was observed at stresses which were lower than the yield stress. The Hollomon's equation very well describes the individual parts of tensile curves for both nodular cast irons including their mutual comparison. From the low cycle fatigue tests, the cyclic hardening/softening curves, the evolution of elastic modulus and hysteresis loop shape parameters, cyclic stress-strain curves and fatigue life curves were obtained for both temperatures and materials. Moreover, the decrease of retained austenite volume was measured by neutron diffraction and the evolution of surface relief was characterized during cyclic straining for both austempered nodular cast irons at both temperatures. On the basis of these results both cyclic plasticity and fatigue degradation mechanisms in relation to the cyclic strain localization were described for both nodular cast irons.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:233891 |
Date | January 2010 |
Creators | Tesařová, Hana |
Contributors | Kohout, Jan, Kruml, Tomáš, Konečná,, Radka, Pacal, Bohumil |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds