The master thesis deals with the influence of heat treatment and storage time on microstructure and mechanical properties of 26MnB5 steel, which is used in the production of tubular components in the quenched and tempered state. The objective was to increase the plasticity of the steel by the definition of new process parameters of the induction heat treatment line. New tempering diagrams of 26MnB5 steel for two various speeds of the heat treatment line were established and used to determine new tempering temperature and speed of the heat treatment line. Observation of the influence of storage time on mechanical properties of the steel did not reveal that it is liable to ageing.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:416434 |
Date | January 2020 |
Creators | Brabec, Martin |
Contributors | Podaný, Kamil, Peterková, Eva |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds