Estudo da incorporação de nanopartículas de prata na matriz polimérica de termoplástico elastomérico poliester (TPE-E) por diferentes técnicas de processamento visando ação bactericida / Study of the different processing techniques of silver nanoparticles incorporation in the polymer matrix of polyester elastomeric thermoplastic TPE-E aiming bactericidal action

A primeira parte do estudo consistiu em caracterizar as amostras de termoplástico elastomérico poliéster (TPE-E) modificadas via irradiação gama (γ) em presença de atmosfera de oxigênio e irradiadas com fonte de 60 Co nas doses de 5, 10, 20, 30, 50 e 100 kGy. Na segunda parte foram realizadas as caracterizações das dispersões coloidais de prata metálica adsorvida em sílica pirogênica (AgNPs_SiO2) e do óxido de zinco aditivado com prata metálica adsorvida em sílica pirogênica (AgNPs_ZnO). Na terceira e última parte, as concentrações de 250, 500, 1000 e 5000 ppm, em massa , de AgNPs_SiO2, idem para AgNPs_ZnO, foram misturados mecanicamente por 30 minutos com 1 % em massa de óleo ALKEST TW 80, 0.3 % em massa de anti-oxidante Irganox 1010 e grânulos de TPE-E, posteriormente processados, independentemente, via injeção plástica, extrusão monorosca e irradiação com prensagem a quente. As técnicas de caracterização utilizadas no trabalho foram: espectroscopia no infravermelho (FTIR), calorimetria exploratória diferencial (DSC), análise termogravimétrica (TGA), difração de raios X (DRX), espectrometria de fluorescência de raios X por dispersão de comprimento de onda (WD-XRF), microscopia eletrônica de varredura com espectroscopia por dispersão de energia de raios X (MEV-EDS), microscopia eletrônica de transmissão com espectroscopia por dispersão de energia de raios X (MET-EDS), índice de fluidez (MFR) e ensaios de tração. As amostras de TPE-E irradiadas apresentaram diminuição da temperatura de degradação (Tonset) e do índice de fluidez (IF) com o aumento da dose de irradiação. Foi possível observar nos resultados obtidos por espectrometria de fluorescência de raios X por dispersão de comprimento de onda a presença de prata nos compostos de sílica pirogênica e de óxido de zinco com sílica pirogênica. Todas as amostras de TPE-E contendo aditivos AgNPs_SiO2 e AgNPs_ZnO obtidas pelas diferentes técnicas apresentaram atividade bactericida para bactéria Gram-negativa Escherichia coli (E.Coli) e a bactéria Gram-positiva Staphylococcus aureus (S.Aureus), sendo os melhores resultados obtidos nos filmes de TPE-E irradiados e prensados com 0.5 % de AgNPs_ZnO com doses de 20 e 50 kGy e 0.5 % AgNPs_SiO2 com doses de 0 e 20 kGy. / The first part of the study consisted of characterizing samples of thermoplastic polyester elastomeric polyester (TPE-E) modified by gamma irradiation (γ) in the presence of oxygen atmosphere and irradiated with a 60 Co source at doses of 5, 10, 20, 30, 50 and 100 kGy. In the second part, the characterization of the colloidal dispersion of silver silicon adsorbed pyrogenic silica (AgNPs_SiO2) and the zinc oxide added with colloidal dispersion of metallic silver adsorbed on silica pyrogen (AgNPs_ZnO). In the third and final part, concentrations of 250, 500, 1000 and 5000 ppm, mass%, of AgNPs_SiO2, identical to AgNPs_ZnO, were mixed mechanically for 30 minutes with 1% by mass of ALKEST TW 80 oil, 0.3% by mass of Irganox 1010 anti-oxidant and TPE-E granules, further processed independently, via plastic injection, monosulfur extrusion and irradiation with hot pressing. The characterization techniques used in the work were: infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray fluorescence spectrometry by wavelength dispersion WD-XRF), scanning electron microscopy with X-ray energy dispersion spectroscopy (SEM-EDS), transmission electron microscopy with X-ray energy dispersion spectroscopy (TEM-EDS), melt flow index (MFR) and traction tests. The irradiated TPE-E samples showed a decrease in degradation temperature (Tonset) and melt flow index (IF) with increasing irradiation dose. It was possible to observe in the results obtained by X-ray fluorescence spectrometry by wavelength dispersion the presence of silver in the silica pyrogenic compounds and of zinc oxide with pyrogenic silica. All the TPE-E samples containing additives AgNPs_SiO2 and AgNPs_ZnO obtained by the different techniques presented bactericidal activity for Gram-negative bacteria Escherichia coli (E.Coli) and Gram-positive bacteria Staphylococcus aureus (S.Aureus), being the best results obtained in the TPE-E films irradiated and pressed with 0.5% AgNPs_ZnO at doses of 0, 20 and 50 kGy and 0.5% AgNPs _SiO2 at doses of 0 and 20 kGy.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-01112018-105111
Date11 September 2018
CreatorsLeonardo Guedes Marchini
ContributorsDuclerc Fernandes Parra, Baltus Cornelius Bonse, Guilherme Wolf Lebrão, Gerson Marinucci, Derval dos Santos Rosa
PublisherUniversidade de São Paulo, Tecnologia Nuclear, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds