Student Number : 0006342N -
PhD thesis -
School of Chemistry -
Faculty of Science / An improved slurry method for determination of PGMs, gold and base metals (Ni,
Cu, Fe and Co) using ICP-OES analytical instrument has been developed. This
method has been successfully applied to quantitate metals in mineral concentrates
and biological samples (grass, lichens, leaves and tree trunks) and validated using
analytical figure of merit that include limits of detection, limits of quantition,
accuracy and precision.
Sample grinding using Fritsch GmbH Pulverissette Planetary Mono Mill was
optimized to get > 60% and >80% of the particles to < 5.0 μm and < 10 μm
respectively. The optimum grinding conditions for a sample mass of 0.4 g was
determined as 130 rpm grinding speed and 30 minutes grinding time. An
additional 15 minutes mixing with reagent was employed to ensure better slurry
homogeneity for improved precisions.
Five slurry dispersants; tetrasodium pyrophosphate, Triton X-100, dodecylbenzene
sulfonic acid sodium salt, potassium cyanide and potassium thiocyanate, were
evaluated at varied concentrations and 0.1% v/v Triton X-100 established as the
best dispersant for slurry preparation.
The ICP-OES sample delivery system was modified by introducing an extension
elbow between the torch and the spray chamber that not only effectively reduced
the sample residence time in the plasma for efficient atomization of the particles
but also acted as a gravitational sieve eliminating larger particles and droplets.
Prepared slurries were continuously agitated using an ultrasonic bath prior to and
during aspiration into ICP-OES to prevent sedimentation and ensure constant
stability of the slurry. Optimum operating conditions for ICP-OES established as 1600 W and 1450 W plasma power for PGMs and base metals respectively, using
a nebulizer flow rate of 0.8 mL min-1, coolant gas flow rate of 13.0 mL min-1,
auxiliary gas flow rate of 1.0 L min-1 with a sample uptake rate of 0.2 mL min-1.
Limits of detection for the developed technique were determined in μg g-1 as
0.075, 0.039, 0.115, 0.071, 0.035 and 0.118 for Au, Ir, Pd, Pt, Rh and Ru
respectively and 0.15, 0.391, 0.345 and 0.217 for Ni, Cu, Fe and Co respectively.
Limits of quantitation in μg g-1 were obtained as 0.250, 0.130, 0.383, 0.237, 0.117
and 0.393 for Ir, Pd, Pt, Rh and Ru respectively and 0.5, 1.31, 1.15 and 0.723 for
Ni, Cu, Fe and Co respectively. Good accuracy was recorded for all the base
metals as well as for the platinum group metals and gold except iridium that was
susceptible to copper interference.
Two measurements of precision, reproducibility and repeatability were assessed.
Reproducibility was obtained in percentages as 12, 7.93, 5.54, 10 and 12 for Au,
Pd, Pt, Rh and Ru respectively and 9.9, 10, 9.8 and 10 for Ni, Cu, Fe and Co
respectively. Repeatability was obtained in percentages as 11, 7.03, 4.94, 8.08 and
9.85 for Au, Pd, Pt, Rh and Ru respectively and 9.4, 9.6, 9.7 and 10 for Ni, Cu, Fe
and Co respectively. Good percentage recoveries were obtained of 104.3%,
98.3%, 98%, 90.5% and 92.8% for Au, Pd, Pt, Rh and Ru respectively. Percentage
recoveries of 109%, 111%, 89.9% and 100% for Ni, Cu, Fe and Co respectively
were obtained.
The simplicity and low cost of sample preparation used in this method enables it to
be easily adopted in any ICP-OES laboratory. A single analyst may achieve more
sample through-puts than before per day (including re-grinding and analysis),
resulting in a highly economical and rapid technique for determination of metals.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:wits/oai:wiredspace.wits.ac.za:10539/2199 |
Date | 02 March 2007 |
Creators | Ochieng, Levi |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis |
Format | 35884 bytes, 35294 bytes, 28291 bytes, 18380 bytes, 11446 bytes, 9958 bytes, 10203 bytes, 27022 bytes, 6444142 bytes, 30744 bytes, 563174 bytes, 973242 bytes, 253943 bytes, 48149 bytes, 9296736 bytes, 16888 bytes, 17301 bytes, 110423 bytes, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf |
Page generated in 0.0101 seconds