TiAlN-based Coatings at High Pressures and Temperatures

TiAlN and TiAlN-based coatings that are used of relevance as protection of cutting tool inserts used in metal machining have been studied. All coatings were deposited by reactive cathodic arc evaporation using industrial scale deposition systems. The metal content of the coatings was varied by using different combinations of compound cathodes. The as-deposited coatings were temperature annealed at ambient pressure and in some cases also at high pressure. The resulting microstructure was first evaluated through a combination of x-ray diffraction and transmission electron microscopy. In addition, mechanical properties such as hardness by nanoindentation were also reported. TiAlN coatings with two different compositions were deposited on polycrystalline boron nitride substrates and then high pressure high temperature treated in a BELT press at constant 5.35 GPa and at 1050 and 1300 °C for different times. For high pressure high temperature treated TiAlN it has been shown that the decomposition is slower at higher pressure compared to ambeint pressure and that no chemical interaction takes place between TiAlN and polycrystalline cubic boron nitride during the experiments. It is concluded that this film has the potential to protect a polycrystalline cubic boron nitride substrate during metal machining due to a high chemical integrity. TiZrAlN coatings with different predicted driving forces for spinodal decomposition were furthermore annealed at different temperatures. For this material system it has been shown that for Zr-poor compositions the tendency for phase separation between ZrN and AlN is strong at elevated temperatures and that after spinodal decomposition stable TiZrN is formed.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-112213
Date January 2014
CreatorsPilemalm, Robert
PublisherLinköpings universitet, Nanostrukturerade material, Linköpings universitet, Tekniska högskolan, Linköping
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeLicentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationLinköping Studies in Science and Technology. Thesis, 0280-7971 ; 1690