Previous issue date: 2009 / Resumo: No presente trabalho obteve-se híbridos de siloxano e b-ciclodextrina (b-CD). Baseando-se na comprovada reatividade das ciclodextrinas frente a grupos isocianatos, sintetizou-se um híbrido de b-ciclodextrina e siloxano, pela reação da b-ciclodextrina com g-isocianatopropiltrietoxissilano (IPTS), formando uma ligação uretana entre o silano e a b-ciclodextrina. O alcoxissilano, posteriormente hidrolisado, deu origem a um material resinoso do tipo polissilsesquioxano (PSS) modificado por b-ciclodextrina. O mesmo alcoxissilano foi também submetido à condensação com poli(dimetilsiloxano) contendo ¿Si(CH3)2-OH em finais de cadeia, dando origem a uma rede polimérica, também de aspecto resinoso, contendo nos nós de reticulação a b-cyclodextrin. Os materiais obtidos foram caracterizados estruturalmente por espectro infravermelho (IV), ressonância magnética nuclear de C (RMN C) e de Si (RMN Si) e análise por difração de raios X (DRX). O comportamento térmico dos materiais foi analisado por termogravimetria (TGA). A capacidade formadora de complexos de inclusão das ciclodextrinas inseridas no polímero PSS-b-CD foi avaliada pela inclusão de fenolftaleína, monitorada por espectrofotometria na região UV-vis e a difusão de água pelo material foi avaliada por ensaios de intumescimento. A morfologia dos filmes dos materiais preparados foi analisada por microscopia eletrônica de varredura (SEM). / Abstract: In this study, hybrid polymers derived from siloxane and b-cyclodextrin (b-CD) were obtained, by reaction of b-CD with g-isocianatepropyltriethoxysilane (IPTS), forming a urethane bond between these components. The resulting alkoxysilane was hydrolyzed generating b-CD-modified polysilsesquioxane resin (b-CD-PSS). The alkoxysilane was also submitted to condensation with poly(dimethylsiloxane) with ¿ Si(CH3)2-OH end groups, giving rise to a resinous polymeric network. These materials were characterized by infrared spectrum, C and Si nuclear magnetic resonance and X ray diffraction. The thermal behavior was analyzed by thermogravimetry. The capability of b-CD grafted in the siloxane polymers to form inclusion complexes was evaluated by the formation of b-CD-phenolphthalein, by UV-vis sectra. The ability of water diffusion into b-CD-PSS film was evaluated by swelling measurement. b-CD modified siloxanes were able to form films and their morphologies were evaluated by scanning electron microscopy. / Mestrado / Quimica Inorganica / Mestre em Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/250486 |
| Date | 14 August 2018 |
| Creators | Abbehausen, Camilla, 1979- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Yoshida, Inez Valéria Pagotto, 1950-, Schiavon, Marco Antonio, Sabadini, Edvaldo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 64f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds