Orientadores: Julio Roberto Bartoli, Humberto Gracher Riella / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-20T23:19:45Z (GMT). No. of bitstreams: 1
Mazzucco_MateusDeLorenziCancelier_M.pdf: 25131087 bytes, checksum: 9d983cb4726735834e67d038fd3a6235 (MD5)
Previous issue date: 2012 / Resumo: Este trabalho apresenta um estudo sobre a relação entre estrutura e propriedades de híbridos de montmorilonitas organicamente modificadas (MMTO) e terpolímero de acrilonitrila-butadieno-estireno (ABS), compatibilizados com o copolímero de estirenoetileno- butadieno-estireno (SEBS) ou de estireno-butadieno-estireno (SBS) preparados via intercalação no estado fundido em extrusora de rosca-dupla. Quatro formulações de híbridos foram propostas segundo um planejamento fatorial de experimentos 22 para estudar o efeito dos fatores compatibilizante (SEBS e SBS) e composição da MMTO (Cloisite 30B e mistura Cloisite 30B+Cloisite 20A (1:1)). A mistura binária de argilas foi proposta para verificar a viabilidade em balancear o caráter hidrofílico e hidrofóbico dos surfactantes destes dois tipos de argilas. As etapas de processamento foram: 1) Preparação de quatro concentrados na proporção mássica de 49,5: 40: 10: 0,5 de ABS/argila/compatibilizante/antioxidante em misturador interno; 2) Diluição para 4% em massa de MMTO; 3) extrusão do composto; 4) Granulação em moinho e moldagem por injeção dos corpos de prova. O efeito destes fatores e suas interações foram avaliados através de análises de difração de raios-X (DRX), microscopia eletrônica de varredura (MEV), microscopia eletrônica de transmissão (MET), termogravimetria (TGA), calorimetria diferencial de varredura (DSC), ensaios de tração uniaxial, resistência ao impacto, flamabilidade e análises reológicas do fundido em regime permanente e oscilatório em altas e baixas taxas de cisalhamento. As análises de DRX e de MET indicaram que os híbridos apresentaram estruturas intercaladas (ABS/20A30B/SEBS) e parcialmente esfoliadas (ABS/30B/SBS), essencialmente na fase SAN dos híbridos. As análises por MEV mostraram morfologias distintas da superfície de fratura na tração para os híbridos com SBS e SEBS sendo o SEBS caracterizado por uma fratura dúctil. As análises reológicas dos híbridos mostraram o surgimento de um caráter pseudo-sólido, com aumento significativo nos módulos de armazenamento e na viscosidade complexa, em especial para os híbridos com SBS. Este comportamento revela uma provável dispersão em escala nanométrica das argilas nos híbridos ABS, seja na forma simples ou mistura binária de MMTO. A resistência ao impacto, de todos os híbridos, foi significativamente reduzida devido às micro ou nano partículas de argila que podem atuar como defeitos aumentando aconcentração das tensões localizadas. Melhorias significativas nas propriedades mecânicas de tração quanto ao módulo de elasticidade foram verificadas nos híbridos com SBS em relação ao ABS de referência, por sua vez os híbridos com SEBS mostraram um expressivo comportamento dúctil. No ensaio de flamabilidade na horizontal (norma UL 94 HB) verificou-se uma supressão do gotejamento de material incandescente durante a queima dos híbridos contendo SBS, gotejamento observado nos híbridos com SEBS e no ABS de referência, este comportamento favorável é provavelmente devido à viscosidade do híbrido fundido SBS ser o dobro do SEBS. O estudo da cinética de degradação termo-oxidativa dos híbridos mostrou que a energia de ativação dos híbridos compatibilizados com SEBS é significativamente maior do que os híbridos com SBS, provavelmente devido à hidrogenação do butadieno no SEBS que melhora a sua estabilidade térmica. O grau de dispersão obtido pelas argilas permite designar estes híbridos como nanocompósitos de ABS / Abstract: The present work, shows a study about the relationship between structure and properties of hybrids of organically modified montmorillonites (MMTO) and terpolymer of acrylonitrile-butadiene-styrene (ABS), compatibilized with styrene-ethylene-butadienestyrene (SEBS) or styrene-butadiene-styrene (SBS) prepared by melt blending process. Four formulations of hybrids were proposed in a 22 factorial design of experiments to study the effect of factors compatibilizer (SEBS and SBS) and composition of OMMT (Cloisite 30B and Cloisite 30B + Cloisite 20A mixture (1:1)). The binary mixture of clay was proposed to verify the feasibility of balancing the hydrophobic and hydrophilic character of surfactants these two types of clays. The processing steps were: 1) Preparation of four masterbatches in mass ratio of 49,5: 40: 10:0,5 of ABS/clay/compatibilizer/antioxidant in an internal mixer; 2) Dilution to 4% by weight of OMMT; 3) Extrusion of the compound; 4) Granulation in mill and injection molding of test specimens. The effect of these factors and their interactions were evaluated through analysis of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetry (TGA), differential scanning calorimetry (DSC), uniaxial tensile tests, impact strength, flammability and rheological analysis at high and low shear rates. The analyses of XRD and TEM showed that hybrids had structures intercaled (ABS/20A30B/SEBS) and partially exfoliated (ABS/30B/SBS) essentially in the SAN phase of the hybrids. The analyses by SEM showed different morphologies of the fracture surface in tensile for hybrids with SBS and SEBS, being the SEBS characterized by a ductile fracture. The analyses rheological of hybrids showed the appearance of a pseudo-solid behavior, with a significant increase in storage modulus and complex viscosity, in particular for hybrids with SBS. This behavior reveals a probable dispersion in nano scale of clays in hybrids ABS, either as single or binary mixture of MMTO. The impact strength of all hybrids were significantly reduced due to micro or nano clay particles that can act as defects increasing the concentration of localized stresses. The mechanical properties showed positive results of tensile as so elastic modulus observed in hybrids with SBS in relation to pristine ABS, while hybrids with SEBS showed a significant ductile behavior. In horizontal flammability test (UL 94 HB) verified a suppression of dripping of incandescent material during the burning of hybrids containing SBS, drip observed in hybrids with SEBS and pristine ABS reference, this behavior is probably due to the viscosity of hybrid melted SBS be the double of SEBS. The study of the kinetics of thermo-oxidative degradation of hybrids showed that the activation energy of the hybrid compatibilized with SEBS is significantly greater than the hybrids with SBS, probably due to hydrogenation of the butadiene on SEBS which improves their thermal stability. The degree of dispersion obtained by clays allows to designate these hybrids how nanocomposites ABS / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266723 |
| Date | 20 August 2018 |
| Creators | Mazzucco, Mateus De Lorenzi Cancelier, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Riella, Humberto Gracher, Bartoli, Julio Roberto, 1954-, Morales,, Ana Rita, D'Avila, Marcos Akira |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 156 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds